I'm 60 next month and back in the day we scrounge everywhere for these parts to no avail. The closest I ever came was a cross boss manifold that takes the trumpet single style, 8 down drafts, but was bare and the carbs were impossible to get so I passed on it, shame never found another one, until you my eyes are wide and I'm a kid again, to see these parts are amazing thank you.

@kellycoffield533

2 жыл бұрын

Thanks Boss Man. The Inlines can still be had......but not cheap. www.inlinecarb.com

Wow.....beautiful work and workmanship! some rare carbs there!

That's a good method to maintain flatness. You really have this down to a science, incredible how thin your castings are for the amount of surface area. Thanks for sharing!

This is another one of the most incredible displays of talent on KZread! I have so many questions on how you do this.

@BedeMeredith

2 жыл бұрын

I wonder if he has an hoa,

@douro20

2 жыл бұрын

@@BedeMeredith It does look like he lives in a covenant community.

@kellycoffield533

Жыл бұрын

@@BedeMeredith I refer any complaints about my driveway casting to the HOA President.....that's me! 🙂

Simply amazing work, you have all us amateur casters jaws dropped! Thank you so much for sharing this 👍

That is a very unique cross ram style intake for upright Weber type carbs, I have never seen this style before, should make for really good low end response.... Outstanding work Kelly!

My line of interrest casting!!! You just got a new sub

Man, I stumbled upon you looking for the actor off of In Living Color looking for a good laugh, and I am so lucky I did, haha!! Love what you're doing!!

Truly amazing Kelly. I've seen video of lost foam casting done in a factory setting, but never so well explained as you have while doing your work. Like it is said, "If you are really good at doing anything, you make it look easy ". You have another fan of your work. Cheers !

Another great job Kelly!! My compliment from an Italian lost foam professional. All the best

@kellycoffield533

Жыл бұрын

Thanks Aldo. Still learning and improving. Best, Kelly

@aldobergamasco905

Жыл бұрын

@@kellycoffield533 Kelly, if you be in need of advice, ask without trouble. I'll happy to help your improvement. For instance ...the rounded vibration flask do not help your effort.

@kellycoffield533

Жыл бұрын

@@aldobergamasco905 I would welcome your input on the flask and also a previous comment you had made about carbon plumes. Not sure YT is the best vehicle to do so. Is there an email address where I can reach you? Best, Kelly

Hands down the best!

Ford Logo look sweet!

Wow that's impressive to see your castings, they look like great1

You never fail to Impress. I bet you're enjoying the CNC now haha. Well done good Sir.

A DOKC-20 21 manifold? I didn't recognize the carb bolt pattern before. (Not 48 IDA Weber). Now I see it's for the Autolite inline 4-barrel. Too Cool!

I like the conical shapes.. my air filter is very thin like yours and I thought of using that idea 20 years ago. Good to someone forming it in trick cast aluminium.

Now I’m getting it , you are the guy that make this engines 👀 look great 😊👍

I've never tried at home metal casting ,but I've watched enough of it on here to know how impressive your results are. The only thing that would further blow me away is if your day job / background was something totally unrelated to mech engineering. Keep up the amazing work and thanks for sharing!!

Damn, you do some pretty work.

Wow! Very inspiring!

Just incredible work! Parts look amazing, you really have dialed in the process. Just had to subscribe!

Amazing work. You are a master of this craft.

Epic series, well done!

I’m impressed.

I've watched several of your casting videos. Amazing almost covers it. Subscribed!

Thanks for sharing. It was great to be able to see how the process works.

Stunning work. Master level.

Beautiful casting as ever! Nice one!

Just amazing! Beautiful work!

That is absolutely fantastic. Very impressive. Thanks for the video.

Thank you for the awesome content Mr. Coffield 👍

Great video as always. Thanks for posting.

Love your work. Love the Ford parts too.

That is truly an amazing talent thanks for sharing.

amazing, very impress work as always, thanks for sharing!

Truly amazing. 😎

Very very impressive video Mr Kelly.you motivate me with your every step .thank you for sharing

Really impressive work! I've been trying to find the actual geometric shape for those cones.. the best I could come up with is pseudosphere or tractricoid

Fantastic work sir. This really makes me want to make a custom one off intake for my car but I also feel I would be stepping on the toes of an individual who did make them for a while. I have the production piece, its just all the lovely core shift and piss poor machining make it unusable. I've been hacking up a stock unit to make work well enough but... I want more lol. Again, fantastic.

I'm amazed

Great work. You should consider inverting 1 of the 'Ford' logos. Then the lid can be installed in either direction.

Super, as usual!

wearing Loafers while pouring 660°C molten Aluminum, that's confidence... :D :D :D

Please make a small 4 liter v10 from Honda parts. If anyone could do it this guy could. Amazing stuff

This is some of the best quality content I've seen on casting complex parts. Have you considered casting an exhaust manifold yet from iron? I'd love to see what you'd do differently with iron rather than aluminum. Thanks!

@kellycoffield533

2 жыл бұрын

No iron yet. Just haven't had any priotrity iron parts but an exhaust manifold would be a well suited part for LF. Would be same process but may require higher refractoriy coating for ferrus work. Best, Kelly

@AccuracySpeaks

2 жыл бұрын

@@kellycoffield533 Could your rig get hot enough to pour cast iron?

@kellycoffield533

2 жыл бұрын

@@AccuracySpeaks Not with the resistive electric heat source, but the refractory insulation is modular and can be converted to a fuel fired furnace in a few minutes. Best, Kelly

I think it would have been unique to have the base and filter housing as one piece, cutting out all the inside, and making a stretch band filter media wrapped around the OD. It would be a work of art

This is alchemy!

Your quality is so good, you should try to get a contract with Shelby America, you could be an authorized provider of OEM authentic parts.

Hello, Your quality of work, and your skill, are quite incredible, and probably unique. You are doing very inspiring work, and I ask myself the following question: is it possible to cast bronze by this process? I am asking you this question because I am thinking of making sailboat portholes in bronze, and your process seems to me suitable for amateur manufacture. Thank you again for your various vodeos, which provoke imagination and admiration, and also for your answer to my question. Be well, and may God give you a long and profitable life. Sincerely, from Normandy

Bravo !

Your work is amazing and I appreciate all of the helpful information you provide others in your videos. You have inspired me to make a Ford 2.3l intake manifold. I have most the foam work done and am working on the gating system next. Do all high points need a gate attachment to avoid air being trapped or will the head pressure fill them from below pushing the air out through the sand? Thank you!

@kellycoffield533

2 жыл бұрын

Lost foam gating is an interesting subject. Gating at high points isn't so much to avoid trapping air, because that occurs through the pattern and coating surface just like the rest of the mold. Moreover, it's to avoid localized mold collapse if the reversing of direction slows the molten metal flow such that the foam evaporates faster than the metal advances. But this isn't always a problem. The downside to multiple contact points on top the pattern is multiple metal fronts must converge into one as they travel down the mold which can lead to defects. Top gating works best if you can contact a massive section on top of the pattern which then tends to naturally spread and feed the entire pattern from top down. This case also produces good directional solidification from bottom up. Another approach like I used on these parts is a long thin contact area the length/depth of the pattern because it minimizes the total distance the metal must flow from the hot/molten metal feed system. I try to keep the cross sectional area of the sprue, runners and gate area similar because if the downstream area becomes too large, the feed system can have a hard time keeping up. But, unlike open cavity conventional sand casting, the lost foam mold fill rate is dictated by the rate foam is evaporated, not strictly gravity and feed system cross section. Fill times on my lost foam molds are usually 2-3x slower than they would be for the same in an open cavity sand casting. Good luck on your intake manifold. Best, Kelly

Awesome

Excellent work, it's good to know people can still do this sort of work. Todays kids would probably look for an app to do it...

Kelly, nice work - and well explained. Regarding pattern making, do you have to oversize the patterns by 5 or 6 percent to allow for a shrinkage factor when the aluminum cools?

@kellycoffield533

2 жыл бұрын

The patterns are 1.3% larger to allow for aluminum shrinkage. Best, K

Hello Kelly. impressive work , the foam patterns are great, is lost wax system similar ? How did you learn 2D cnc ? I want to m/c a flat pattern with multiple curvature, very similar to what a camshaft lobe would look like, but 300 mm / 12" diameter. can you suggest any Y/T tutorials etc .... ta robbie NZ

Thanks for the content, great stuff. I've seen others commenting on the audio, which sound muffled on most of the videos I've seen so far. Are you using an action camera with a sealed weather case around it? It sounds like the microphone is covered up by something. Edit: guess not, the muffled sound comes and goes.

@kellycoffield533

2 жыл бұрын

It's because it's an old phone mounted behind me on a tripod so I am speaking away from the speaker. Admittedly the audio isn't great, the finned cylinder casting video is the worst, but I can easily listen to all of them on every device I own with volume up. I guess I'm more interested in casting than making spiffy videos and am more likely to attract a like minded group of viewers. K

Hey Kelly, thank you for all of the videos! Can you give us some information of where you get your lost foam casting material at?

@kellycoffield533

2 жыл бұрын

I have a video on the subject if you search my channel for "materials". Best, Kelly

Parabens gostei

Love the content, very interesting. Can you do these patterns with 3d printing and do a sort of lost PLA casting?

@kellycoffield533

2 жыл бұрын

No. There were supposedly a couple companies working on such but expnaded polystyrene foam is feather light and the filament would need some kind of foaming agent which I'm sure would be very hard to control expansion. For now, it's cuttings with the CNC router instead of additive printed construction. Best, Kelly

You might want to consider putting a removable lift arm on your molding cart to lift the extension up so you don't have to fight with it as you did on this one.

That looks great, i worked in a foundry for about one year, everything was done with green sand, so what i see here is there is no binder in the sand, the aluminum just displaces the foam without the sand falling in, really that i would not think possible, i looked in your videos but did not see you go into what the sand is, looks like dry playground sand, i think i need to try this. thanks for your effort.

@kellycoffield533

2 жыл бұрын

It's just 50-70 mesh silica sand, washed, and dried. Typically used for mortar mixes and available at the big box stores. Not play-sand. That stuff sucks. I have close friends that are life long foundrymen that owned their own foundries. Years ago, when I first started lost foam casting, I invited them over, showed them a foam pattern with cores and voids, undercuts and backdrafts, and, told them what I was going to do to mold and cast it. They just shook there head and said, "I thought we taught ya better". When the casting came out of the sand there was a long period of silence before convesation ensued once again....🙂 Best, Kelly

@zenvent

2 жыл бұрын

@@kellycoffield533 What is your favorite foam to use for detail? Just insulation sheets?

@kellycoffield533

2 жыл бұрын

@@zenvent Yes, Owens Corning Foamular 150, the pink stuff available at retail stores. Foamular 250 os slightly more dense and will finisnish slightly better at the expense of having to evaporate modestly more foam. Both work well for most lost foam parts. Dow has similar material. Theirs is light blue. The color is just branding/marketing. Best, Kelly

Beautiful cross-boss parts. Will you be doing the single-quad intake as well?

@kellycoffield533

2 жыл бұрын

Maybe! Best, Kelly

Amazing quality of work there. I found your channel by accident just trolling youtube. Question: How do you "treat" your aluminum ? What I mean by that is, do you degas the molten aluminum and if so how ? Do you do anything else to "treat" the aluminum ? The reason I ask is because I have done a very small amount of casting but each time it appears that the aluminum is porous. It has almost microscopic amounts of "voids" (for the lack of a better term). It then becomes weakened. When you buy a piece of round stock from the machine shop it's perfect but if I pour my own it's not the same quality. Your casting appear to be perfect. Thanks for any replies.

@kellycoffield533

2 жыл бұрын

For the last couple years I've used A356 Ingot in a resistive electric furnace and I dont degas. When I used to recycle a lot of scrap metal, I did degas with argon with a lance I made. If you have a fuel fired furnace keep the burn lean and the pour temp as low as possible to fil your parts and you will minimize porosity. Best, Kelly

@canadianoddy8504

2 жыл бұрын

@@kellycoffield533 Thank you very much for the reply. Yes I do use scrap aluminum. Specifically pistons, left over AL from my shop, etc. It's all clean stuff. Thanks for that tip on low pour temp.

how small of a piece can you make? Very interesting technology.

@kellycoffield533

2 жыл бұрын

In theory there is no limit as to how small but in practice, the ability to produce acceptable detail and finish on the foam pattern is the limiting factor. So for simple parts, maybe 1/16 thick by 1". If I was making jewlery or artwork, I'd use lost wax or 3D printed pattern media, and either investment or shell casting. This will reproduce finer details and finishes. But for larger machine parts, IMO, lost foam is much less laborious, more versatile, practical, and economical for small quantities and home hobbyists. Best, Kelly

I hope you don't mind restating this question, which type of foam do you use? Thank you Sir, very fine skill and excellent teaching. Take care

@kellycoffield533

2 жыл бұрын

Owens Corning Foamular 150. It's 1.3lb/ft3 extruded polystyrene insulation board available at the home improvement stores. I have a video on pattern construction materials with more details. Best, Kelly

Amazing work! In your CAD designs, do you account for shinking in the aluminum? for example, do you say model the part to the exact dimensions, then scale everything up by % when you export to CAM?

@kellycoffield533

3 ай бұрын

Yes, I CAD model 1:1 and do the scaling in the CAM program increasing the size by 1.3% to account for shrinkage. Best, Kelly

@thegenrl

3 ай бұрын

@@kellycoffield533 thank you for sharing all you have figured out over the years.

How much weight did you lose after making the second one thinner?

can you radius the inlet on the base plate?

what kind of glue do you use for your foam patterns?

How hard to adapt to the taller deck height Cleveland/ Boss 351? The Pantera guys would buy every one, especially with the Autolite inline carbs. Hell, I'd buy a Pantera just to show off one of your induction systems.

@kellycoffield533

5 ай бұрын

Already done. Look at these two videos. kzread.info/dash/bejne/q4Gmz8epmsa0YZs.htmlsi=ssVVgh9PvtiW7pX6 kzread.info/dash/bejne/n6Wmy7iNnN2tmcY.htmlsi=hgT_gL_mazGYWNZK Best, Kelly

GOOD كم تكلفة المشروع

Beautiful work! Do you need to make the mold oversized for any shrinkage? Im thinking about giving this a shot to recast a component thats no longer available and some of the dimensions is critical. Thanks.

@kellycoffield533

2 жыл бұрын

For aluminum I make the patterns 1.3% (.013" per inch) larger to account for shrinkage. Best, Kelly

@JohnClutch1

2 жыл бұрын

Thank you for your time, Kelly. Maybe once I get the part laid out, Ill share it with you.

Hi there, With the lost foam method is there more porosity with the end result casting, as I noticed in one of your vids you talked about sealing the parts with Loctite. I deal with the sand casting system via the local foundry and don't have lots of porosity, occasionally but not to bad. is there ways to off gas the parts more effectively, just wondering. Thanks for all the videos

@kellycoffield533

2 жыл бұрын

In general, I'd say LF is no more or less prone to porosity. IMO, most of the issues with porosity are related to aluminum, it's affinity for hydrogen and H2 related porosity, and general melt management to prevent such. If done properly, lost foam may actually be less suspectable because none of the byproducts of decomposed PS Foam are soluable in molten aluminum and the mold media sand is dry (no binders to emit gases that are soluable in molten aluminum). The downside of LF, is it requires a slightly higher pour temp and the solubility of hydrogen is a function of temperature, but IMO this is a very minor difference. For melt management, I use a resistive electric furnace. It is very clean, there are no hydrocarbons present, and the furnace atmosphere is most likely inert. Best, Kelly

@kellycoffield533

2 жыл бұрын

In regard to vacuum impregnating castings, I use to use a lot of dirty scrap and remelt. It was harder to get that metal gas free. I built a good degassing lance and those issues ceased. I also poured hotter in those days which likely wasnt helpful. I've since started using virgin ingot and do not degass, and have had zero issues since, so the loctite hasnt seen the light of day since. Best, Kelly

I would like to put that on my 65 mustang 289/306

Put ya a vee band clamp on the bottom of your mold hopper and let the sand fall out the bottom.

Kelly, Are you still using a low temp hot glue gun? Great parts by the way.

@kellycoffield533

2 жыл бұрын

Yes with the lowest melt temp glue I can find, for the quick sticks. For longer work time I use various forms of PVA glue, but all as sparingly as possible. Best, Kelly

Just curious....on the manifold pours..did you have enough v-moulds to pig the whole crucible if the main mould went south?

@kellycoffield533

2 жыл бұрын

No, I only had about 30lbs of ingot tray provisioned, but if necessary, the crucible could have been returned to the furnace while the first round of ingot froze. Best, Kelly

@larryanderson8049

2 жыл бұрын

@@kellycoffield533 LOL I figured you would have something figured out incase....all of your work seems to be well thought out....you seem to be a good guy to learn from....the comments show that!

Hi Kelly! Is your furnace DIY or is it a commercial product?

@kellycoffield533

Жыл бұрын

I built it from scratch. Best, Kelly

Can you please tell us what the matrial/s you are using for the coatings, dipping?

@kellycoffield533

8 ай бұрын

Search my channel. There is an entire video dedicated to coatings. Best, Kelly

Is there any foam you can use that can be poured into a cavity??

@kellycoffield533

2 жыл бұрын

Not that I'm aware of. The commercial operatins use pre-expanded beads in metal molds and then us steam to expand and bond those into patterns. It's a pretty involved process easily as complex as the rest of theprocesses combined. Two part epoxy and urethane foams do not work well. No printed materials that will burn out like foam either. Best, Kelly

If you dont mind I'd like to know what you use for the refractory coating and roughly the cost I'm looking to cast an engine block and cylinder head and need something to get my foam patterns with

@kellycoffield533

2 жыл бұрын

I use REFCOTEC PolyCap 600. There is a 600lb minimum buy and will set you back $600 so best to find someone to share the cost. Drywall joint compound will work nearly as well for aluminum, is very inexpensive, and commnly available. Best, Kelly

@lukeamato2348

2 жыл бұрын

@@kellycoffield533 awesome thanks so much. I'm just looking to cast aluminum anyways. You think plaster of Paris might work? Like in a slurry

@lukeamato2348

2 жыл бұрын

@@kellycoffield533 I was considering g trying my own mix to test. Probably a bottle of Elmers glue and plaster of Paris mixed with water

@kellycoffield533

2 жыл бұрын

@@lukeamato2348 If you thinned itto the right consistency, yes. But dry wall mud (nonsetting joint compoubd) the additives that make it better for joint compound also make it better than just PoP for a lost foam refractory coating. Better in respect to surface coverage, dryinng, and permeability. A thin coating (enough to turn pink foam white) is sufficient. Thicker doesnt necessarily mean better. Best, Kelly

Would it not be easier to lift the extensions off with a crane?

@kellycoffield533

3 ай бұрын

With the long lever handle on my molding rig I've actually found that I can control the dump just fine with the extensions so that's what I do. Best, Kelly

And what kind of refractory coating did you put on this model?

@kellycoffield533

2 жыл бұрын

A commercial product called REFCOTEC Poly Cap 600. But if you search my channel for a video "Refractory Coatings for Lost Foam Casting Patterns" I discuss thta and the use of drywall joint compound. Best, Kelly

@user-th5rr2ni6o

2 жыл бұрын

@@kellycoffield533 Can I link to this video? Thank you in advance.

@kellycoffield533

2 жыл бұрын

@@user-th5rr2ni6o kzread.info/dash/bejne/fpibqc2qps6bncY.html

Is licensing an issue when casting the parts as long as your not selling the parts for profit?

@kellycoffield533

2 жыл бұрын

Probably so but I'm not offering such for sale, just my own personal use so I dnt think Henry will feel too threatened. Best, K

@shakeydavesr

2 жыл бұрын

@@kellycoffield533 I don’t know about that,,,,, I heard he could be a son of a gun,,,, may have it done from beyond the grave just to prove anoint,,,,,lol. LOVE this stuff, Been interested for years, never realized lost foam could be done "at home" so to speak. This is freaking awesome.

So would you be interested in making a manifold for me? The ford manifold is very close to my poly 318 intake, there is no aftermarket manifolds for my motor, I have an old cris craft marine manifold that looks similar to the one you created , if you might be interested I'd like to discuss my idea?

@kellycoffield533

2 жыл бұрын

If you're only armed with an idea, not likely. The reverse engineering of the diemsional layout and features takes a lot of time. The cost of doing that and writing the CAM program are very large compared to cutting the pattern and casting it. Interest will vary depending on the project, but realistically, for me to consider it, someone would need to have a surface model for the pattern ready to cut on a 3-axis cnc router. Best, Kelly

Kelly do you do commissions ? How can I contact you ? Thanks

@kellycoffield533

2 жыл бұрын

contact info at www.inlinecarb.com

@______5293

2 жыл бұрын

@@kellycoffield533 Did you get my email?

@kellycoffield533

2 жыл бұрын

@@______5293 At the moment I have many emails and I can no longer see your KZread ID so hard to say. Best, K

Cannot believe that you have Autolite inline carbs , you travel down dark roads .

@kellycoffield533

2 жыл бұрын

I collect, buy, sell, and build systems for them www.inlinecarb.com Best, Kelly

I can never hear your audio,love the vids but volume is too low.please increase.cheers mate

10:39

pls fix your audio Kelly

@shakeydavesr

2 жыл бұрын

Audio is the only issue I have.