I’m a retired certified welder, 41 years worth, and my first welds were in HS shop class in the mid 70’s using 6013. After graduating and starting my career, it was all 7018, most of the time vertical up or overhead! I only do occasional “friends & family” welding nowadays, and I’ve gone back to my roots - using 6013 & 7014 instead of low hydrogen due to the storage issues of 7018 when not using them up steadily. Slag inclusions have always been an issue with 13’s & 14’s, but I stumbled on a great tip! On one of those welding channels from India (you know the ones!), I noticed this guy doing the obligatory dab dab dab 6013 weld along with an occasional standard uninterrupted stringer bead, ALL of them free of slag pockets!! He was using a greenish colored electrode that I figured was some regional thing. I commented, saying how impressed I was with the lack of discontinuities in his beads, I myself constantly fighting it! His response? Get some ESAB 6013’s! My local welding supply didn’t stock them, but got some for me. Opening the first tube of “Sureweld 6013”, I was greeted by the first green welding rods I’d ever owned, and my skepticism was quickly squashed upon burning the first one! I’ve tried 5 or 6 different brands of 6013, but these things are in a class all by theirselves! I highly recommend trying them for yourself! A game changer for me! Excellent video by the way, even though I had to watch it with the sound turned off! Ha!

@trevorslater2746

Жыл бұрын

Hi Tom thanks for the comments, I got my basic welding ticket 30 plus yrs ago but didn't keep it up ,just doing farm,home jobs ,guys was selling strata 555s ,bought them $75 30 something yrs ago ,big $$ then but best rods ever ,finally used the last one ,but being eking them out ,don't know the $$ now would glue anything together, rusty etc

@bonniedobkin6948

Жыл бұрын

That is because ESAB INVENTED SHIELDED RODS , BEFORE THAT THEY WERE BARE METAL 👌

@shanerogers2835

Жыл бұрын

I just came across one of the best deals absolutely ever . Lockheed Martin was selling off a tone of old equipment. I bought 3 flammable storage lockers full of welding equipment welding rods wire gloves all sorts of tools for $150 a piece I bought three of these lockers . Each one of these lockers was chalked full of these 3/32 golden rods. Golden is the name of them as the color of them. My machine is a Miller bobcat 225. These rods seem to be a 5p type rod the only thing is when I weld flat with them it leaves pits not sure what the deal is I'll be laying a really nice roll of dimes and then something happens the slag breaks away or something I don't know it just leaves a crater but like I said it's only when I will flat a pill in overhead beautiful beautiful beach. Do you have any suggestions

@tomt9543

Жыл бұрын

@@shanerogers2835 The undesired crater or slag inclusions scream out 6013 or 7014 to me, but I’ve never seen “Golden” electrodes! If there’s no number on them, it’s hard to figure out what you’re dealing with! There is a “Golden Bridge” manufacturer of welding consumables in China, and they list two different versions of 6013: J421 (J38.12) E4313, and J421X E4313. If that’s what they are, flat beads can be very frustrating, and rely on rod angle, travel speed and amperage. Welding too “cold” can cause those defects, running hotter gets everything stirred up and separates the molten puddle and slag better, and letting the molten slag get in front of the puddle is a sure sign that the weld will be full of discontinuities! 6013 & 7014 are typically not used vertical up or overhead because of the heavy slag, but it could be that out of position welding uses gravity to pull the slag away from where it’s not wanted! I can’t be sure though because I’ve never used either uphill or overhead!

@shanerogers2835

Жыл бұрын

@@tomt9543 ok this electrode is a 3/32 on the side of the road it says " X-ERGON #106 DURA-WELD GOLD. . these rods are a chocolate chip cookie, golden brown with very small specks of white and little bit of black . The exposed end of the rod ,that you stick into the stinger is an ugly shade of almost cheap spray paint gold.. unfortunately these rods didn't come in a box or can , just a sealed plastic bag, no MSDS no markings on the bag . Each bag is 25 maybe 30 lbs I have in all 71 bag's. Thank you so much for your information. I've never had trouble like this with 7018 , 6011, 6022 , or 6010s it's quite frustrating. I've been a structural steel Ironworker for 24 years, never busted out on any weld test or inspection. Normally when I burn rod , my slag peal's off .

Just bought your 4 pack bundle, looking forward to getting stuck in! I was a mig welder on a production line for 2 years, 20 years ago. Looking forward to learning the knowledge behind the skill as back in the day it was just practice until you get good, never mind the theory 👍

As a hobbyist getting into welding, your videos have been immensely helpful. By far the most clear, concise and to-the-point videos.

Tim is without doubt the best tutor on KZread.. Since I started welding a few years back I've learnt everything from this guy

Old timer here. I had problems for a long time with 6013s. The problem was I kept trying to use it like a 6011. Remember you need a gap when using a 6011 and others. Try dragging the rod with no gap or very little. You'll see the difference. For many years all I had was a Lincoln AC buzz box. I have learn things to use that others don't talk much about. Like rod manipulation and watch the heat versus what people say the amp dial says. Think more like an artist than an weld engineer. Loosen up, get comfortable. It's a great day when your welds look good. Then the welding bug will get you big time. If you are not having fun burn more rods til you smile 😀

You’re the clearest, most concise welding instructor on KZread. Subbed!

Just started welding recently. Watching your videos has helped me immensely. My boss even said my welds are nicer than his and he has been welding 30+ years so i thank you for that.

HI Tim, Jose from Puerto Rico. I'm 65 years old and retired, but I've always been interested in learning to weld. As much so that I've taken a basic stick welding course just to get my feet wet, and I truly enjoyed it. Then I stumbled on your channel, and I'm at awe of your tremendous skill set and manner of teaching. You're a gifted teacher. Do you think that your course described on your channel would be something I could really learn from? Or do you think that going to school is the way to go? I mean, the price of your total course is mind-boggling exceptional, compared to what I paid for that basic course.

I gave up 6013, but I may have to revisit the rod after watching this video. Appreciate it Tim . . . your delivery seems more natural now....keep up the good work Sir!

HUGE HELP! I'm a beginner and I've been running into this more than anything else. Can't wait to try what you showed here. Thanks!

I have been welding for 35 years but have very little experience with AC electrodes. The struggle is real. Thank you for reaffirming what I subconsciously knew to be true.

This is the most instructive video about this matter (which is my most common deamon) I`ve seen. And the duration of 5 minutes is perfect

Thanks for making this video. When searching for beginners videos on welding this one really is the one that tells you what you need to know to start making good welds with 6013 and really that is all you need to know.

Great video. I had the same issue with 6013. I’m off to the shed to put your advice into practice. Thanks Tim.

All I can say is Thanks Mate from a novice Auzzie welder. Another great and highly useful video.

Great advice and video. Wish I knew this years ago; it would have helped eliminate a lot of inconsistently I have been experiencing exclusively when running slow on 6013 fillet welds!

Ohhhhhh thanks for this vid. I was having the same issue using the 6013. I will check my amperage and weld angle next time. =)

This was a great video Tim, Clear and concise, and very well explained.

You are a great teacher, Tim!

From 🇵🇭...i always watching your vids.new idea.new Knowledge..shout out

Dude, thank you I was getting the exact same results as the viewr that sent you the email Gonna try your tips tommorow. Thanks Tim

I have had similar issues when I weld 6013. I've done a decent amount of welding in a class room setting to figure out what welding mistakes I am making at home. When I work with 6013 try to hold it start of the world for about 1 or 2 seconds then start running a beed. I got a hint from another channel a while back they suggested maybe putting you travel angle a little farther forward to help push the slag away from the weld puddle with 6013 and it seem to help a lot what I was doing. Now I was mainly practicing at home keep up on welding. But good video I like it I love your channel

I'm lucky finding this channel. I have the same problem like this. Thanks man.

Thank you so much sir, i had this problem for a long time when i'm doing corner joint welding 6013 is amazing for every joint except corner and lap joint. Please do more of 6013 electrode content since it is rare content also 6013 is very popular in africa and Asia. Lots of love from Somalia🇸🇴❤

Thanks, this helps a lot, in the town I live in, you only get 6013, nothing else, and I am struggling to get a nice weld.

cheers Tim, I have seen this from time to time in my welding, good to know why. Like a lot of hobbyists 7018 isn't for me, 6013 for most of my work, it can be long periods between welding and rods need to be able to sit for months if not years open on the shelf, and be fine to use straight away - which 7018 cant do.

Thanks for the hot tip. 6013 is what’s available here in Australia so any advice is always appreciated regards Ardy

Hi Tim, thanks for helpful reply to my email and I appreciate you taking the time to make a video addressing the issues I am having using 6013 rods. In the UK they seem to be the only welding rods on the shelf plus the do not need to be stored in an oven like the 7018s. I have not applied the tips you have given me yet but I will let you know how it goes when I do. Cheers

@MyGFIsMaria

Жыл бұрын

Here in Europe we often use ISO instead of AWS so for example ESAB OK 48.00 is the same as 7018 and I found it on the UK version of ebay. But 6010 is hard to find here.

@yewsengcheong1637

Жыл бұрын

Thank you for requesting this. It was the exact same problem I was having but didn’t know how to ask it. I often get welds onto one side and not the other and slag inclusion. I need more amp and steeper angle and I think I need to slow down too!

@jimjungle1397

Жыл бұрын

I noticed when I was in Europe 6013 was popular there for home welders, but here in America, it seems 6011 is much more popular for home use.

@safetyfirstintexas

Жыл бұрын

@@jimjungle1397 6011 is the no prep rod for welding junk steel mill scale ,and anti rust coating. a almost universal rod!

@robertmintz63

Жыл бұрын

@@MyGFIsMaria 6011 is the same as 6010

Coming from Mig/TIG, I struggle with this issue the most. It’s often frustrating and heartbreaking. Thanks for the insights, I’ll give it a shot.

I recently purchased your online course, and have completed stick welding. You should add this as a troubleshooting step! I was having this issue in every fillet and some lap joints, it would have been easier to have it included in the lessons vs having to research it elsewhere. But overall I like the course and learned (but not mastered) stick quickly. Can’t wait to start on the shielded processes though, slag and smoke suck!

I wanted to learn welding for a long time ; so I have been watching Tim's videos for a while now . I got myself a cheap Inverter DC welder 2 weeks back and been practicing with some 2.4 mm and 3.15 mm 6013 electrodes . I found that with 70-75 amps I get good results with the 2.4 mm 6013 electrode ( or at least it seems good to me , lol ) and 100 to 110 amps with a 3.15 mm 6013 electrode . I need to work on my welding angles and travel speed ; it's only a fortnight I have been welding :)

@usernamemykel

Жыл бұрын

I was a fortknight who couldn't fight well with a sword, but was good with a crossbow.

Thanks, this is why I switched to 7018 as my go to rod. The 7018 restart issue I deal with by keeping a small file handy and I file the end clean of flux before I restart.

Thanks Tim, you’re a great educator.

Hi Tim, The first time I learned to weld was when I was 7 years old, and over the last year, I became burnt out from 25+ years of software engineering, and one of my friends told me - "Dave, have you tried working with your hands again?" Your channel has helped me so much, and I thank you for it! You keep up the good work! This. Is. Awesome. Oh - I'm starting an official welding course next year ;-)

@chriswf

6 ай бұрын

I know that burnout. I craft that time when I get to work with my hands. I can't leave software, as I don't think I can make as much with my hands at my skill level. But working with my hands is way better.

Your videos are really awesome. There are so many variables that can have a profound effect on making a good solid weld from day to day or even throughout the day or night. HOWEVER, this usually involves temprature and moisture, in my experience. I spent 5 years welding where every weld and weld repair was UT'd or Mag. Part.tested with the outcome also noted in your record as a passed or failed weld. I moved from the Midwest (Hot and Humid) to a High Desert environment which is very Hot with very low humidity) during the day. I transferred to nightshift and on one night, I had a small 6" repair to make on 3/8" mild steel at a depth of 3mm. on a weldment that was stored outside after it failed Ultra Sound. I had brought the section inside the plant and guickly gound the slag inclusion and poracity out. As i started to fill in the gash, the supervisor came by and told me to slowly preheat the steel up a little bit in that area, if i valued my record. When i asked him WHY it was necessary. He stated because of " moisture in the metal from condensation, even though it's dry to the touch and eyes, it's " wet ". It will also prevent cracking and warping from thermal shock so don't chance it". I fired up the belch fire torch and saw the moisture being driven out almost right away. The canyon i ground out filled up so nice, that i didn't have to butter up the weld and it passed. From that time to this day i preheat everything from 1/4" on up. Even if the outside humidity is only 20% at 70 degrees. Just another one of if those little details that can make a difference.

@Ihaveausernametoo

4 ай бұрын

Hadn't even considered this. Thank you!

Brilliant insight. I always use 6013 and experience exactly this problem

@thisisyourcaptainspeaking2259

10 ай бұрын

I'm pretty sure I don't have any 6013 because of this problem.

Thanks Mr. Tim, truly you solve the issues in E - 6013 electrode, Godbless!

Wow, amazing lesson. Thank you, much appreciated!

Great channel Tim! Thanks for all the tips.

Many tanks! Solved my 6013 problem :). God bless!

Thank you, all the best to you and your loved ones

Good video man. Those are some awesome tips thanks and keep the videos coming

You have saved me from bad welds with 6013. I usually bump it 7-10 degrees hotter and makes a difference.

Had this *exact* trouble today with *Forney 7018AC!!!* Turned current up, gave it more angle…

When I weld thicker plates ( like 1/4"), I use 105 or 120 amps on my old Lincoln AC with 6013. I get lots better results than at low amperage. I also find that weaving from side to side for the first half inch or so, leaves a more uniform weld.

Very helpful video. Thanks for posting it.

Thanks Tim, I needed that. Cheers Stuart 🇦🇺

Thanks for the videos, finally I found the way out 🙏

Well explained, keep up the good work!

Great video. Thanks Tim!

Very well explained, thank you very much.

Thanks Tim, Informative and succinct.

Great video, thanks Tim 👍

Thank you Great demonstration

I’ve found arc length is important with 6013 rods, really tightening it up seems to help blow the slag away from the puddle for me. There’s also (certainly here in Australia anyway) a difference between brands, some are a lot smoother running than others. A bloke I was working with was giving me tips on my welds, he’s very picky about which brand he’ll use and it certainly helped me.

@fuckingpippaman

Жыл бұрын

the tighter the arc the better (if you have enough amps)

@glennh2965

Жыл бұрын

Mate, So what are the best 6013 here? Not Bunnings I'm guessing...

@Oldtanktapper

Жыл бұрын

@@glennh2965 Don’t think they’re the best, but the Bossweld from Bunnies aren’t actually too bad. They’re the ones my welder mate told me to go with, they lay a decent bead.

@samwhite1823

11 ай бұрын

Absolutely right. Steep work angle, tight arc and you should be able to feel both plates with the flux as you feed the rod. Those 2.4mm really burn off quick too

@samwhite1823

11 ай бұрын

I use Oerlikon Fincord M, they are the most butter smooth rod when you get used to them. Could weld in a shirt and tie with them

That's so helpful mate! Thanks ❤

Thanks Tim I got your website and will be in contact. Have a great day.

Yeah ace Tim nice to have some good commentary rather than other vids with no explanation like on most youtube vids out there

Nice information Tim. Thanks for continuing to make quality training videos. Something to consider on future videos is taking a still frame of ‘good’ and another of ‘bad’, and putting them onscreen next to each other. Even better would be drawing some curved lines on the stills showing where the arc defining line is and also the edge of the weld puddle. After you’ve been welding a while, these are easy to see. But people new to welding may not understand where to look. When you show a video and say, “as you can see…”, those of us that have been welding a while can of course see what you’re talking about. But somebody that’s just starting out may not be able to pick out the details.

@yewsengcheong1637

Жыл бұрын

Yes! I have been looking everywhere to see this cause I don’t know what I should be looking for.

@rpavlik1

Жыл бұрын

Yeah a little drawing on the arc shots would be nice

@schweinnase7138

Жыл бұрын

I agree as well. A break/snapshot an some hand drawn lines with different colors for slag and weld pool will make this explanation perfect. Maybe direkt in this video as an overlay? Thanks Tim for sharing your experience.

Thank you ! 🙂 Excellent demonstration ! Literally, from all angles 🤗 👍 ♥️ 🍻 🦘

Can you do a video on welding at awkward angles? In your shop/bench setup, you always weld at “ideal” positions: top down, flat surface. Can you do vertical and even upside down angles? Thanks. Your channel is awesome

@TimWelds

Жыл бұрын

I can work some more of that in, for sure. Thanks!

Thanks for very useful video.

Great info… very practical

Thank you, have had this problem with 6013 and, as others have said, worked out for myself that upping the amps and adding some rod angle seemed to sort it out, good to have this technique confirmed.

Awesome tutorial as always, Tim. Same problems for me with 6013...can't see puddle, trapped slagged, undercut if I turned up the heat, etc. On my own I stumbled on increasing the travel angle. But real, the best solution for 6013...is to switch to 7014 haha!

@rivernet62

Жыл бұрын

Exactly my thought. If you can work with a clean surface, why would you mess with 6013.

@timlong1462

Жыл бұрын

I found the same thing. I learned on 6013 and thought I was just bad until I switched to 7014. It is better in every single way.

@jefffrayer8238

Жыл бұрын

Same here. I'm just welding on the farm but never been able to make nice welds with 6013. I can make nice looking welds with 7014 and never had one break. I use 1/8 and sometimes 3/32. 7014 keeps years for me, stronger than 6013 and lays a nice bead so I don't see any reason for 6013. Great video.

@PercyJackson93

Жыл бұрын

Would this still be within about a 10-20' travel angle? I've been trying a lot to get rid of porosity in my welds even with 7018

Very well explained.

I could actually really see the difference here. Not sure which line was the one you were talking about as the clearly-defined puddle, but I did pick up a small box of Harbor Freight 7018 to practice with during the course, then I'll come back to my massive box of name brand 6013.

Great! Have been having this exact same problem. Could you have lines on still images to show what we should be looking for and what not please? Maybe a what to look for for various types of common electrodes please?

You just helped me so much 😂

Well that answers my question 👏🏻

nice video sir. i would like to ask. during 3g welding, the upper beads (closer to the top/end of the plate) seem to have more thickness than the lower ones. why is that, whats the solution. thank you

Here in South Africa one only gets the 6013 on shelves.Different manufacturers and are they a pain in the but and on top of that one has to weld 1.6mm and 2mm steel with it when making safety gates.I thought I was a terrible welder cause I sometimes have the same problem of slag caught up in weld.Currently I weld at 77Amps and not much of a problem other than blowouts.Thanks for sharing.Currently doing a 6meter gate a 3.4m gate and a 1.18m gate with 1.6mm rectangular tubing and 10mm square steel.

讲的非常棒，正在学习，谢谢

I feel like I've seen another 6013 troubleshooting video on TIm's channel but as someone who's only working with 6013 so far, I've done the mistake on the thumbnail so countless times as I was learning on my own. On 6013 fillet welds you really have to make sure that the starting puddle and arc has warmed up and stabilized well, and keep the arc length really close! That's one thing not mentioned in this vid for the issue, I'm guessing arc length got a bit too long and the arc and deposits were just going everywhere. Keeping the arc length small makes it so that the deposits only go where you want it to, and that's critical for a rod where you don't have as much puddle visibility as other rods

@phasis97

4 ай бұрын

yea im pretty sure he could have summarized the video in 2 seconds: dont long arc, increase drag. once ur in the correct amp range its just a matter of travel speed

Thank you!

Good job! Could plz make a video on welding steel disk to steel rod.

Good video brother

I learned more lesson today that i will never forget thank you sir; may God continue to bless you 🙏 please sir how do I take follow you on line

Nice one Tim, thank you. On some future video, could you maybe edit a picture of a welding in progress to show that boundary between the weld pool and slag, please? Not obvious to me with the 6013, not sure what I should be looking at. Rookie here hey 👋

@robertmintz63

Жыл бұрын

The slag should not exceed past the middle of the puddle . If you use an auto lens adjust so you can see the slag running around on the puddle . If you are using a regular green lens #11 then go to gold leaf (it blocks mor UV rays) & drop to #10 , that is all I ever used to use

Thanks & im interested in the online course

Trying to do some plug welds with Stick and I keep getting undercut/slag stuck in the plug. It’s a real pain where I don’t think rod angle will help. Anyone able to offer any advice? Love the videos Tim, very informative and well put together.

I have been welding for over 50 years. Granted, for the past 5-8 years my oscillation is built in, but I always watch what my puddle is doing. I use 6013 often and 7018 as a primary rod....I love the stuff. What I have noticed is that if you are running the weld on either and it is running downhill, even slightly like a few degrees, the slag on 6013 tends to run over the puddle. Keep the welds even or uphill and you will do away with a lot of that puddle problem.

I worked in Todd's Shipyard in Seattle in the 80's and they had the best welders I've ever seen, stick, tig and mig. I moved to Baja 12 years ago and asked around for a good welder. I was told that a fellow in town was the best around. I needed a header for my truck fixed and the job was so bad I ended up spending $500 for a new set. Everything is so half assed down here, I now have only certain people do my repairs but it's taken a long time to learn the ropes. I've been screwed multiple times and they don't even use Vaseline.

I learned more lesson today that i will never forget thank you sir may God continue to bless you 🙏 please sir how do I take follow you on line

Hi Tim, awesome watch. Quick one, would like to find out, what mm is the rod you welding with?

Thanks very much

This happens to me a lot. I have a 110v 100 amp buzz box, so can't turn up the amperage. The most I can do seems to be 3/32" 6013. I'll try the steeper electrode angle next time.

How important is electrode storage for 7018 if I'm just a go-kart building, backyard hobbyist?? Thanks in advance! 🙂

Thanks

I have to use 6013 in all positions I run them on DC- turn the amps up a tad and touch down slag peels leaving a very nice flat micro rippled bead. DC+ = Arc blow for what I weld.

Just today was 6013 welding some 1-5/8" pipe 1/8 thick and had that problem. I'll try increasing the stick angle tomorrow to see if that helps. Did not want to turn amps up to 90 because of pipe thickness. Since i'm welding around the circumference of the pipe, keeping the stick angle constant is a challenge.

Great tuition, thamkyou, I've been making some gates for the last few days and have started feeling like I've got the flu, could it be the welding

Hi 👋 how long does it take for you to finish your ear to ear as for me it took me 3 day s thank u , my work absolutely changed after watching your videos ❤

Brilliant thanks Tim. I run beautiful beads on 8mm plate when practicing, but doing internal corners has always tripped me up. This demo of 2.6mm on 3mm steel is great for real world (backyard 🙂)

@PercyJackson93

Жыл бұрын

Can I ask what you used for the 8mm plate? 3.2 or 4mm?

@glennh2965

Жыл бұрын

@@PercyJackson93 3.2mm. Should I try some 4mm?

@PercyJackson93

Жыл бұрын

@@glennh2965 I'm fairly new to welding so trying to sort out a few problems. I've been doing fillet welds on 8mm flat bar and grinding down again square and I've found it very difficult to get penetration with the weld. A thicker rod of 4mm is recommended but I've still to try it. A thicker rod will have more penetration but more heat for warping as well.

Can 7018 rod that has been sitting out for years be improved. I was thinking of drying them in an oven.

I do 60 amps on a 1/4 and weld really good up

Can I run 7018 with my 220 AC unit? Aka tombstone welder. I'm getting similar results with 6011 and 6011E. I can use 6013 but my work looks like it puked all over the welding area. I normally run at 90 to 105 amps but last job I moved to 120 amps with better results. No schooling in welding, just bench work education. What am I missing? Thanks

you have taught me so much in five videos... CHEERS MANNN!! YOUR FUCKING AWESOME!!💥🕉️

I still do a fair bit of welding using 6010 , 6013, 7018 and I am relatively easy using any of these . I have some esab stainless rods as well . I sometimes even now get a bit of slag inclusion because I weld very thin metals and as you would know stick and paper thin metals don’t really like each other

The best 6013 rods are MUREX VODEX as they weld over anything and are also brilliant positional rods with no undercut