How to get Gold and silver from ceramic CPUs and ICs. Special thanks to Venca Bílek for 2 CPUs :-)
Жүктеу.....
Пікірлер: 52
@justinjackson9705 Жыл бұрын
Nice! Never gets old watching gold precipitate. It's a thing of beauty. Nice pure gold you got.
@BohumilGraman
Жыл бұрын
Thank you :-)
@chosen1one930 Жыл бұрын
I think it's funny when people don't convert silver chloride first and just melt it as is lmao. Good work as always and good information
@BohumilGraman
Жыл бұрын
Thanks
@lukasblazek5225 Жыл бұрын
Nadhera, jsem rad, ze videa opet vychazeji casteji.
@BohumilGraman
Жыл бұрын
Děkuji ;-)
@art1muz13 Жыл бұрын
Good work as always and good information
@BohumilGraman
Жыл бұрын
Thank you ;-)
@johnbackes2266 Жыл бұрын
A work of art
@BohumilGraman
Жыл бұрын
Wau :-D
@chosen1one930 Жыл бұрын
Will you do a video on the caps, I just enjoy watching your content glad to see another video from you
@BohumilGraman
Жыл бұрын
Yes :-)
@escrapchannel Жыл бұрын
Perfect result 🌟 🌟 🌟 👍
@BohumilGraman
Жыл бұрын
Thanks ;-)
@chosen1one930 Жыл бұрын
Do you know which cpus to be on the look out for? Or know what sample cpus are? I got 3 engineering samples on ebay for 52.50, 2 486 pretty early in development, these are worth close to $1,000. The 3rd is a extremely rare 487 SX but before it was named that, that's how early in development it was, it could be one of the first engineering samples but these are beyond rare to begin with. The highest offer on the 487sx ES to date is $6,000 but it staying in my collection for now
@BohumilGraman
Жыл бұрын
I only process normal and damaged processors. The interesting ones and in good condition remain in my collection, they are worth much more than just gold.
@chosen1one930 Жыл бұрын
I just remove the caps with heat and process the gold plated ones separately. The cpus with exposed dies like amd duron, Thunderbird and Athlon ceramics don't need to be broken if anything process those separate because no gold is inside those chips only the pins.
@BohumilGraman
Жыл бұрын
Yes, it´s right ;-)
@8bitrainbowdash18 күн бұрын
Damn, I wish I could do this at home, have a bunch of cpus and work at a electronics scrap place, but I do not have the rom for the fumes or risks.
@ghostprotocol5876 Жыл бұрын
Delicious content🤝🤝
@BohumilGraman
Жыл бұрын
Thanks ;-)
@tomtichi8760 Жыл бұрын
Awesome
@BohumilGraman
Жыл бұрын
thx
@MiguelSierra Жыл бұрын
Excelente.
@BohumilGraman
Жыл бұрын
Thanks ;-)
@boortutkun4507 Жыл бұрын
iyi çalışmalar kolay gelsin
@BohumilGraman
Жыл бұрын
Yes, thanks ;-)
@mbsmgmail Жыл бұрын
Nice Master
@BohumilGraman
Жыл бұрын
Thanks
@mrmek2003 Жыл бұрын
Super...
@BohumilGraman
Жыл бұрын
Dík ;-)
@purusottamadas4314 Жыл бұрын
Velmi dobrá práce, jen tak dál. Kde ten materiál pořád bereš? 🙂 Za 7 let se mi podařilo nashromáždit hodně elektroodpadu, ale když vidím tvoje videa, tak si říkám, že mám prdlais. Přeji všechno nejlepší do roku 2023.
@BohumilGraman
Жыл бұрын
Děkuji :-) Jak je příležitost, tak do toho jdu, takže skoupím celou starou ústřednu (viz video), nebo kontajner vysílaček... :)
@lightning-rods Жыл бұрын
What is in the solution that turns red when smb is added? It was at the first drop when smb us added
@BohumilGraman
Жыл бұрын
I don´t know, maybe SMB reaction with residual of HNO3?
@lightning-rods
Жыл бұрын
@@BohumilGraman I've had it happen to me a couple times. I thought it might be iron/ steel or some base metal. But it's never happened before on any of your videos or any of the other sites that have done a first refine and a second refine. So it leads me to believe it could be a different precious metal. Once you finished the second refine and drop, there was still color in the left over solution. Could that be some left over precious metals? Have you ever thrown some copper in the solution to se if some more precious metals would drop out of solution? Thx for your reply. Your videos are great and the content is real helpful. Keep up the great work!!!
@aryatajally8909
Жыл бұрын
Use high concentrate NH4Cl if solution is red, if anything precipitated that may be Pt
@MIRAE_GOLD Жыл бұрын
Good
@BohumilGraman
Жыл бұрын
thx
@frantiseklaluch6605 Жыл бұрын
Zdravím, výsledek nádherný, ale kde se proboha ještě dneska dají sehnat tyhle historické procesory... to musel někdo dlouho sbírat... 🤔
@BohumilGraman
Жыл бұрын
Děkuji. No nějaký pátek jsem to dával dohromady :) Jsou to jenom špatné kusy, ty hezké jsem si samozřejmě nechal, mají mnohem vyšší cenu, než pouhého zlata...
@franguimfrangoso104 Жыл бұрын
Salve salve guerreiro 💎⛏️🇧🇷
@BohumilGraman
Жыл бұрын
:-D
@user-yu5ol5vz7q24 күн бұрын
Лайк тебе и подписка 👍🔥
@kubik_rubik1537 Жыл бұрын
Krása. Jsem velmi rád za větší frekvenci videí. : ) Tento postup se mi líbí více, než rozpouštět napřímo v LK. Jaký je prosím poměr a koncentrace H2SO4 a HNO3? A jaké je cca množství na kg materiálu? A ty pozlacené "víčka" se prosím zpracují jak? Všude se zmiňuje, že se dělají separé, ale postup jsem ještě neviděl. Také v LK, jen se déle rozpouštějí a proto se dělají samostatně? Děkuji za info a přeji spoustu kvalitního materiálu i v dalším roce.
@BohumilGraman
Жыл бұрын
Děkuji :) H2SO4 35 %, HNO3 35 %, já používám poměr 1:1, ale není to exaktní. V tomto případě jsem použil cca 2 l roztoku. Víčka se odleptají ve směsi H2SO4 a HNO3 a čisté folie se rozpustí v LK. Udělám na to video ;-)
@kubik_rubik1537
Жыл бұрын
@@BohumilGraman Děkuji za rychlou odpověď. Ještě jedna věc (teda jedna z mnoha) mi vrtá hlavou: jak při kyblíkových metodách zjistit, že je všechno zlato rozpuštěno? V létě se chystám vyzkoušet nějaké kovové tranzistory, které mají různý poměr kovu, keramiky, atd. a tak bych nerad plýtval chemií, stejně jako bych nerad přicházel o zlato. Zatím dělám jen piny ve skle a tam jde hned vidět, kdy je hotovo.
@BohumilGraman
Жыл бұрын
@@kubik_rubik1537 Je to o odhadu. Prostě naliji tolik, kolik myslím, že bude potřeba a po reakci přeliji do jiného kýble. Pokud je hotovo, neřeším, pokud není, naliji zpět a přidám ;-)
@nasranim Жыл бұрын
Závidím ti ten borax, že nepění ten co mam já pod plamenem skoro uteče z misky...
@BohumilGraman
Жыл бұрын
:-D
@CanadianTreasureHunter Жыл бұрын
Nice Gold But You should of saved the rare Ceramic ic's, Worth way more than the Common Gold you got
@BohumilGraman
Жыл бұрын
I only process damaged processors, I keep the nice ones in my collection, they have much more value than the gold in them.
Пікірлер: 52
Nice! Never gets old watching gold precipitate. It's a thing of beauty. Nice pure gold you got.
@BohumilGraman
Жыл бұрын
Thank you :-)
I think it's funny when people don't convert silver chloride first and just melt it as is lmao. Good work as always and good information
@BohumilGraman
Жыл бұрын
Thanks
Nadhera, jsem rad, ze videa opet vychazeji casteji.
@BohumilGraman
Жыл бұрын
Děkuji ;-)
Good work as always and good information
@BohumilGraman
Жыл бұрын
Thank you ;-)
A work of art
@BohumilGraman
Жыл бұрын
Wau :-D
Will you do a video on the caps, I just enjoy watching your content glad to see another video from you
@BohumilGraman
Жыл бұрын
Yes :-)
Perfect result 🌟 🌟 🌟 👍
@BohumilGraman
Жыл бұрын
Thanks ;-)
Do you know which cpus to be on the look out for? Or know what sample cpus are? I got 3 engineering samples on ebay for 52.50, 2 486 pretty early in development, these are worth close to $1,000. The 3rd is a extremely rare 487 SX but before it was named that, that's how early in development it was, it could be one of the first engineering samples but these are beyond rare to begin with. The highest offer on the 487sx ES to date is $6,000 but it staying in my collection for now
@BohumilGraman
Жыл бұрын
I only process normal and damaged processors. The interesting ones and in good condition remain in my collection, they are worth much more than just gold.
I just remove the caps with heat and process the gold plated ones separately. The cpus with exposed dies like amd duron, Thunderbird and Athlon ceramics don't need to be broken if anything process those separate because no gold is inside those chips only the pins.
@BohumilGraman
Жыл бұрын
Yes, it´s right ;-)
Damn, I wish I could do this at home, have a bunch of cpus and work at a electronics scrap place, but I do not have the rom for the fumes or risks.
Delicious content🤝🤝
@BohumilGraman
Жыл бұрын
Thanks ;-)
Awesome
@BohumilGraman
Жыл бұрын
thx
Excelente.
@BohumilGraman
Жыл бұрын
Thanks ;-)
iyi çalışmalar kolay gelsin
@BohumilGraman
Жыл бұрын
Yes, thanks ;-)
Nice Master
@BohumilGraman
Жыл бұрын
Thanks
Super...
@BohumilGraman
Жыл бұрын
Dík ;-)
Velmi dobrá práce, jen tak dál. Kde ten materiál pořád bereš? 🙂 Za 7 let se mi podařilo nashromáždit hodně elektroodpadu, ale když vidím tvoje videa, tak si říkám, že mám prdlais. Přeji všechno nejlepší do roku 2023.
@BohumilGraman
Жыл бұрын
Děkuji :-) Jak je příležitost, tak do toho jdu, takže skoupím celou starou ústřednu (viz video), nebo kontajner vysílaček... :)
What is in the solution that turns red when smb is added? It was at the first drop when smb us added
@BohumilGraman
Жыл бұрын
I don´t know, maybe SMB reaction with residual of HNO3?
@lightning-rods
Жыл бұрын
@@BohumilGraman I've had it happen to me a couple times. I thought it might be iron/ steel or some base metal. But it's never happened before on any of your videos or any of the other sites that have done a first refine and a second refine. So it leads me to believe it could be a different precious metal. Once you finished the second refine and drop, there was still color in the left over solution. Could that be some left over precious metals? Have you ever thrown some copper in the solution to se if some more precious metals would drop out of solution? Thx for your reply. Your videos are great and the content is real helpful. Keep up the great work!!!
@aryatajally8909
Жыл бұрын
Use high concentrate NH4Cl if solution is red, if anything precipitated that may be Pt
Good
@BohumilGraman
Жыл бұрын
thx
Zdravím, výsledek nádherný, ale kde se proboha ještě dneska dají sehnat tyhle historické procesory... to musel někdo dlouho sbírat... 🤔
@BohumilGraman
Жыл бұрын
Děkuji. No nějaký pátek jsem to dával dohromady :) Jsou to jenom špatné kusy, ty hezké jsem si samozřejmě nechal, mají mnohem vyšší cenu, než pouhého zlata...
Salve salve guerreiro 💎⛏️🇧🇷
@BohumilGraman
Жыл бұрын
:-D
Лайк тебе и подписка 👍🔥
Krása. Jsem velmi rád za větší frekvenci videí. : ) Tento postup se mi líbí více, než rozpouštět napřímo v LK. Jaký je prosím poměr a koncentrace H2SO4 a HNO3? A jaké je cca množství na kg materiálu? A ty pozlacené "víčka" se prosím zpracují jak? Všude se zmiňuje, že se dělají separé, ale postup jsem ještě neviděl. Také v LK, jen se déle rozpouštějí a proto se dělají samostatně? Děkuji za info a přeji spoustu kvalitního materiálu i v dalším roce.
@BohumilGraman
Жыл бұрын
Děkuji :) H2SO4 35 %, HNO3 35 %, já používám poměr 1:1, ale není to exaktní. V tomto případě jsem použil cca 2 l roztoku. Víčka se odleptají ve směsi H2SO4 a HNO3 a čisté folie se rozpustí v LK. Udělám na to video ;-)
@kubik_rubik1537
Жыл бұрын
@@BohumilGraman Děkuji za rychlou odpověď. Ještě jedna věc (teda jedna z mnoha) mi vrtá hlavou: jak při kyblíkových metodách zjistit, že je všechno zlato rozpuštěno? V létě se chystám vyzkoušet nějaké kovové tranzistory, které mají různý poměr kovu, keramiky, atd. a tak bych nerad plýtval chemií, stejně jako bych nerad přicházel o zlato. Zatím dělám jen piny ve skle a tam jde hned vidět, kdy je hotovo.
@BohumilGraman
Жыл бұрын
@@kubik_rubik1537 Je to o odhadu. Prostě naliji tolik, kolik myslím, že bude potřeba a po reakci přeliji do jiného kýble. Pokud je hotovo, neřeším, pokud není, naliji zpět a přidám ;-)
Závidím ti ten borax, že nepění ten co mam já pod plamenem skoro uteče z misky...
@BohumilGraman
Жыл бұрын
:-D
Nice Gold But You should of saved the rare Ceramic ic's, Worth way more than the Common Gold you got
@BohumilGraman
Жыл бұрын
I only process damaged processors, I keep the nice ones in my collection, they have much more value than the gold in them.