Pulse MIG vs Short Circuit
#welddotcom
An episode on pulse MIG vs short circuit
Head over to our Website and become a free member: www.weld.com
You can join our groups and forums, ask technical questions, answer questions in the community, look for jobs and more!
Follow up on Instagram: / welddotcom
Visit our www.Weld.com/shop
Don't miss new episodes of our podcast, please subscribe and leave us a review!
Now available on these platforms:
Anchor: anchor.fm/welddotcom
Google Podcasts: www.google.com/podcasts?feed=...
Spotify: open.spotify.com/show/4qWd24Y...
RadioPublic: radiopublic.com/welddotcom-6N...
Breaker: www.breaker.audio/welddotcom
Brands that Support the Channel:
BOHLER WELDING: www.voestalpine.com/welding/
ABICOR BINZEL: www.binzel-abicor.com
ESAB POWER SOURCES: www.ESAB.com
EVERLAST POWER SOURCES: www.everlastgenerators.com/?r... AHP POWER SOURCES: www.ahp.com
COMEAUX CAPS: comeauxcaps.com/
Get your ISOtunes (OSHA / NIOSH Compliant) Headphones HERE: And Use our code WELD10 for 10% off isotunes.com/?rfsn=3712318.e7...
TubeBuddy: www.tubebuddy.com/welddotcom
Disclaimer: As an Amazon Affiliate and influencer, Weld.com earns from qualifying purchases via our posted links and affiliate links.
Videos produced and made available by Weld.com or any of its affiliates, subsidiaries, or representatives (collectively, "Weld.com") are provided for informational purposes only. Although every effort has been made to provide the most accurate and useful information from sources believed to be reliable, no warranty, expressed or implied, is made regarding accuracy, adequacy, completeness, legality, reliability, or usefulness of any information. As tools, products, materials, equipment, techniques, and applicable laws, regulations and ordinances are constantly changing, Weld.com cannot and does not assume any responsibility or liability for the accuracy of the information contained herein. Under no circumstances shall Weld.com be responsible or liable in any way for any content, including but not limited to death, injury, errors or omissions in the content, or for any loss or damage of any kind incurred as a result of any content communicated in a video, on a website or by other means, whether displayed by Weld.com, or a third party in its original or a modified form. All content is subject to Weld.com and any third party's applicable terms and policies. Carefully review all terms and policies.
ALWAYS USE CAUTION WHEN UTILIZING ANY DISPLAYED TOOLS, EQUIPMENT, TECHNIQUES OR PROCESSES. IF EVER IN DOUBT, CONSULT A LICENSED PROFESSIONAL. ANY RELIANCE ON THE PRESENTED INFORMATION IS STRICTLY AT THE VIEWERS OWN RISK. EACH VIEWER EXPRESSLY AND VOLUNTARILY ASSUMES ANY AND ALL RISKS INCLUDING, BUT NOT LIMITED TO, DEATH, DISABILITY, AND/OR SERIOUS PHYSICAL INJURY RELATED TO THE USAGE OF ANY TOOLS, EQUIPMENT OR TECHNIQUES OR PROCESSES IN THE PRESENTED CONTENT. IN THE EVENT OF AN INJURY IMMEDIATELY SEEK MEDICAL ATTENTION.
Пікірлер: 110
Valuable information as always :) Weird audio cut out when you where talking about the gas.
@jimandskittum
3 жыл бұрын
Speaking of gas, what was that noise around 7:06?
@oSKIIBOWSK1o
2 жыл бұрын
@@jimandskittum Hahahaha was thinking the same thing
I used to run 100s hard wire in pulse mode at the shipyard. The navy wouldn’t let us use flux core on big ut butts vertical up. We could only use 100s wire in pulse mode. We used 95/5 gas. I’d love to see you do a 3 inch thick vertical butt double bevel and gouge out the back and weld it out and then ut it to see how it comes out. 0.45. Not 0.35. Just like to see it as I had to retire early due to cancer treatment issues. I beat it. Not looking for sympathy just would really like to see a video on that. Have a great day. Love all your videos. I’d like to add it was only certain steel types that we couldn’t use flux core.
If you pause the video and draw straight lines down through both cut and etch lines, the short arc seemed to actually penetrate slightly more than the spray transfer.
@JamesZJi
4 ай бұрын
Based on every video i saw, Short circuit always have more pen on the side wall. Spray has more into the root direction. Only destruction test can tell the truth.
Pulse helps with vertical down on thin gauge steel. I make shelfs when going vertical. Good video!!!
I've got an Everlast pulse mig welder but never tried that feature. What a great video with a clear explanation.
Another great video Jason great information. It’s nice to see using the two different techniques and how it performs with the different gases keep them coming
Great video. Keep them coming, especially the ones on pulse GMAW!
I like the triangle technique for uphill. Good call.
Great video with great info. Thanks for taking the tome to share. Cheers
This is AWESOME! Just dropping off a Knowledge 💣
You guys should do a demo on how to mig weld exaust tubing.
Great compare. Keep em coming!
can you run vertical up spray with fcaw-s or does the vertical fcaw-s penetrate well enough with short ckt or globular
Thx. Question: little confused about your settings. When you changed to pulse what was the difference in settings vs non pulsed
Can you do a video about accu pulse welding versus short circuit? We mainly use accu pulse while at work and only use short circuit to uphill or fill in gaps thanks and great video
Great video you should do more vids covering pulse mig both steel ss and aluminum
I normally run spray downhill and use the arc force to keep the puddle in place so that enough penetration occurs.. never seen anyone manage uphill spray
Using spray vertical is very much doable but you need to manipulate your puddle a lot to get a good looking weld and that makes you sacrifice penetration in your root.
Great stuff as always,. Here is a question, l dont have the posibility to change gas, should I move to Flux core for 3/8 and up? Greetings from Argentina
You can spray overhead fillets. I have to do it for my job
I just started a job welding 1/4 inch ar500 steel we use .45 wire and I’m having a really hard time getting my welds to properly fuse both sides. Can you do a video to help?
Can you show outside corner joint on 1/8", downhill pulse?
We ran overhead w/spray and had no troubles. It was only out of convenience- and what I mean by that is instead of taking 15 mins to move the part around with the jib crane, we’d just run it overhead. But, I see what you’re getting at here.
So is short circuit acceptable for thicker material if they are beveled and you run stringer beads?
Wait so how did you run spray in the first flat fillet weld using 75/25? Or did I miss you switching out the gas for that
Those everlast machines are great. They are the best bang for your buck out there.
Is there an advantage one way or the other between GMAW-P and FCAW-G. Seems like the flux core with gas can perform the same as the pulsed spray? and you wouldn't need to invest in a machine that has a pulse option. The added cost of the flux cored wire would seem to be offset by the lesser cost of running straight CO2 in lieu of the higher percent argon mix.
why you did not use the triangle technique for uphill on short circuiting?
What’s interesting is when you went vertical in spray made it started short circuiting 🤔
I’ve been able to spray in the overhead (4F) position but I have to really keep my travel speed up
@randyharris6527
3 жыл бұрын
It can be done absolutely. Steeper push angle and quick whip n pause
I'm SO PROUD OF YOU GUYS... always using PROPERLY your PPE! Too good for all of you and very educational to ALL OF US!
Thanks for the info. LARRY MOORE
Can we control bead height 2 - 2.5 mm in CMT mode by using. 100 Argon and1.2mm dia wire in cladding
Hey, I've been wondering in a production setting running 1/4 steel and thinner on non structural applications is there a benefit to running pulse over short circuit other than post weld cleaning? Is it possible to run pulse downhill on thin and thick metal without lack of fusion?
@hodgepodgeenginerd1258
3 жыл бұрын
Pulse is the preferred mode for all welding in my shop (Lincoln welders and rapid arc for vertical down). In house we recommend pulse over short circuit for all applications unless we have to use metal core, too many guys cold lap short circuit because we aren’t given time to clean scale. We make dump trucks out of ss, gr50, and mild steel. We ran pulse vertical down for years before we found out it’s “not recommended”
@kevobrando95lx44
2 жыл бұрын
You might have issues with cooking your thinner material but fusion shouldn't be an issue. Pulse atleast on the machines I've used run hotter and faster wire. You set the arc length rather than wire speed, real weird but definitely nice flat solid welds coming from pulse.
You used a different pattern on the short circuit than you did on the pulse, but didn't explain why, or if that had anything to do with not getting into the root. It also looks worse, because the pulse was done first, and pulled the piece to that side, leaving a slight gap for the short circuit side. All that said, it looks to me the short circuit actually had deeper penetration. Could you explain why you used a different pattern, and maybe try it again doing the short circuit first, then the other side to compare apples to apples?
Esab rogue 180, Miller thunderbolt 160, Lincoln century, everlast 200. what’s the best of the best portable stick welder in the $600 range? Your opinion, greatly respected. What you think? I’m leaning towards the esab.
How bout using 100% Argon with 70s6 wire?? How does that work out??
So on the short circuit side the fit up wasn’t as tight as the pulse side since the pulse side was done first and pulled a small gap in the other side. So it’s kinda not apples to apples. Looking at the acid etching, the penetration depth actually looks to be similar, but it wasn’t measured, we were just going off optics. I like the pulse though, so much cleaner.
Say you had to weld thick material out of position and you were stick welding it say it was 5/16th thick if you ran a 5/32nd rod and multi passed it it would be enough right?
@mattfogarty8144
3 жыл бұрын
I ask this because the only time I myself am gonna weld metal this thick would be doing mobile repair most likely and I'll be setup for stick welding also wouldnt it be best to bevel this if I'm really worried about punching into the root? Just wondering thanks jason always appreciate when you do a video you explain things really well verbally and under the hood
What if you whip it forward then back like you would with stick? Give it a chance to freeze then come back to continue the weld. Just saying
Happy Birthday Devil Dog!
Question: If I need to weld an 1/16" or 1/8" wall tubing to 1/2" plate or thicker. Is it okay to short circuit MIG or should I stick weld it? Do I set the machine for the thinner material or something hotter? I know it will weld into the thinner material fine but will it penetrate the thicker material enough? I have a Lincoln 210 mp so I cannot spray. I run 035 wire , c25 gas. Just my home projects. Welding legs onto a plate to make an anvil stand. I usually go hotter and direct my heat into the thicker metal but maybe that is wrong.
@hodgepodgeenginerd1258
3 жыл бұрын
You can mig this just fine. Aiming into the thicker stuff is right. Grind the scale off to improve penetration. I’d turn the machine down enough to keep from burning holes in the tube.
@GaryForgingOn
3 жыл бұрын
@@hodgepodgeenginerd1258 Thank you. I will do that.
Unfortunately, I can only get 80 cu ft tanks because of no delivery to a residential area, and, well, that’s what fits in the car. So it’s argon and ar/Co2 75/25. They won’t fill anything else in that size tank. So what are the best options for 3/8 to 1/2? Multi pass of course, but stick isn’t really my thing.
From a hobbiest stand can using spray transfer (82% argon be beneficial when limited to 110 input voltage
@sunrisetacticalgear29
3 жыл бұрын
No, because you won’t have enough voltage, which I believe is 24-25 volts minimum.
does pulse mig work with 75/25... I used it like that in school and it sounded and looked just like the one you ran with the higher argon mix, was wondering what the difference in pulse mig is like between the two gases.
@Mike-lt6sj
6 ай бұрын
Not spraying
Good comparison. However... a spool of E710 and maybe a couple tips are a lot more affordable than a new welder. Maybe a comparison between dual shield and pulse MIG is in order? Also, your uphill technique leaves room for improvement.
Yeah i have no idea what you're talking about, I realize now that I know nothing about welding in general lol
Im new at mug welding but have been stuck welding for years and have been looking at the Miller 235 and just wonder what your thoughts are on the everlasting?
@geraldgenchur5133
3 жыл бұрын
I was asking his thoughts on welders. If you didn’t have anything to add then why did you reply
@everlastgenerator
3 жыл бұрын
If you're on FB join our group. There's lots of guys in there that can tell you all about our machines.
@everlastgenerator
3 жыл бұрын
@Wroger Wroger the gentleman didn't ask about specs. He asked for a testimonial. I gave him an area where he could get many. If he asked a technical question I would've been more than happy to answer.
@marklugo6002
3 жыл бұрын
@Wroger Wroger Obviously, you need to learn something about MIG/GMAW welding. Wire speed and Amp control are the same exact adjustment. The wire speed and diameter/type of wire determine the amperage delivered to the weld. If you were a true MIG welder, you'd know this. You cannot have separate controls for wire speed and amperage. They can be measured and expressed differently, but it is the same exact control. Everlast, incidentally has several basic MIGs and has for many years. But if you were more than a drive by poster, you'd know this. This MIG answers a need in the auto industry for welding on newer and more exotic forms of Aluminum that are being used. It also has a setting for MIG brazing for high carbon steels. If you knew what you were talking about, you'd have said nothing. It was demoed with steel, but shines really with aluminum.
@marklugo6002
3 жыл бұрын
@Wroger Wroger LOL. Don't even know the basics about welding, or what the controls do and you are building your own machines? And you are trolling Everlast?
Can you still do vertical pulse spray on the thick material like 1” on a miller350p? Anyone want to drop quick settings
@philanderingwhitecollartra8281
3 жыл бұрын
In one pass??? LoL Just run stringers...
Nice. 👍🏻
Just curious, spray mig on thin material such as sheet metal?
@MikeP350
3 жыл бұрын
You'd blow straight through sheet metal with spray.
Why does the millermatic 220 splatter like hell on plulse mig with 035 on c25. I get super nice clean flat welds, great penetration but the splatter is wild and I hear all the time pulse is supposed to have anti splatter qualities
As a new makerspace club cost is a major concern as we put together a metal fab shop on a budget. We are thinking tig/stick because it is awesome but argon is spendy. I think we can tig braze with nitrogen. They use nitrogen as shielding gas in a couple different situations. What about tig brazing with pure nitrogen? 50/50 mix? Would Mr. tig demo this maybe?
Can mts 225 lighting spray mig?
They say coke is addictive.... But i tried pulse mig once and it's over... Now i just pulse everything.....i cannot stop. I don't want to stop!
I would like to see a video something like this one where I can’t go to specialized equipment. I am what you would call a bit more than a hobby welder. I work out of a small garage. At my age 70 it would be stupid to go buy some specialized equipment. I weld with a Lincoln 210 MP. Now for this particular application I would tack one side, back gouge the joint and weld it up, then back gouge the other side and weld it up. This would give me a full penetration joint. What’s you’re opinion? In my opinion this would allow me to properly do the job without investing in new equipment and using what I already have.
@hodgepodgeenginerd1258
3 жыл бұрын
Kinda depends on how much time your spending with extra prep work compared to what is needed with the special equipment.
@timothyrouse2853
3 жыл бұрын
What you doing is fine ? Or of one edge just grind 45 degree before welding , do a root run then a top run ?
Could you guys please do some videos on multi pass fillet welds. Vertical up and vertical down, short circuit transfer with er70s6 75/25 on some 12mm steel (1/2”) I would greatly appreciate it guys
7:51 you see that the T join is not perpendicular.The first weld pull the other piece to it and open a gap for the second weld.I don't belive this test was very nice
Can you use tig without gas and a filler rod?
@ShainAndrews
3 жыл бұрын
I'd like you to think about your question and come back with theories to support why it will and why it will not work.
@NemesisRTCW
3 жыл бұрын
Without filler rod yes, without argon or helium gas No
@ShainAndrews
3 жыл бұрын
@@NemesisRTCW Teach a kid to think and he learns for a lifetime...
@asherdie
3 жыл бұрын
Try with a stick welding rod.
@3:30 Well, i find spray to be real smooth for overhead fillet's (PD/4F), give it a try, just adjust your angle.
👍👍
When I went to trade school we always had to do a root run for the vertical up weld. A good welder should be able to set the welder to out perform the pulse welding process.
Question on mixing gas. To avoid buying a third tank-can I mix my 100% argon with my 75/25 to make the equivalent of 90/10? What type of valve would I need and what would pressure settings be ? Might make a good episode if it hasn't already been addressed in previous videos.
I still don’t really understand the difference between spray and pulse?
Audio cut out 1:57 to 2:08.
Are you in Florida?
Would be intereresting to compare the Pulse Process to normal Spray Process in a Horizontal Position, with a cut and etch! Good Content as always!
Ok so I run pluse might on a Lincoln 360 mp and by the way its sounding your not doing it right at all. You are supposed to run in a stringer like method and gotta have a steady hand. I'm not sure how I can post a picture or a video of me performing the pluse mig metal transfer but if you give me an email I will email you them
And 90 10 gas performs alot better
You've proven that just because a weld looks good it does not mean it has penetrated. Can you guys do a video to see if an ugly weld will still pass?
So you Guys Weld Steel with MIG(inert Gas)? Interesting. We Weld Steel MAG active Gas 82 Argon 18 co2
2nd, but a 3rd class welder.
"And burn again". I always have that resolution but most of the time I can't make it
I understand you are professional but I'm a hobbyist and I really can't afford to change gas rental bottles for each project
@ypaulbrown
3 жыл бұрын
Some suppliers will let you have cylinder for free for 30 days. Then charge rental monthly after that....
@ShainAndrews
3 жыл бұрын
Then you select a process that meets 80% of your needs. How often you weld thicker than 5/16"?
@bruced1429
3 жыл бұрын
try some dual shield flux core , you can use 75/25 or even 100% CO2 . 035 wire will do most jobs to 3/8 in (1/2 in with 045) and there is little smoke as compared to self shielded flux core and with the dual shield you can weld in any postition to max the metal size you do need at least a 200 amp welder
Im having a hard time knowing the difference. I only hear a difference.
thnx for video🙏 Hi from Russia🇷🇺🤝
The circut weld was been terrible.
1st
wait, who is this guy is he new?
@Syltibob
3 жыл бұрын
He's the original gangsta. But the youtube-fame and money has him spending all his time on his yacht with a bunch of hoes. That's why we rarely see him.
@anilramlogan8737
3 жыл бұрын
Lol I was just kidding.. First time I've seen him since he cut his beard.
@anilramlogan8737
3 жыл бұрын
@Wroger Wroger lol I always wondered if it wasn't a fire hazard 😅
marine take a clean shave