Making a highly swellable hydrogel | Swelling and Temperature Sensitivities effect Comonomer Content
Polymer Hydrogels which have different amount of comonomer vinylsulfonic acid VSA were synthesized. Swelling capacity and Temperature sensitivity are examined. Biomedical materials, polymers, polymerization reaction, ATRP, solution polymerization, stimuli responsive hydrogels, smart polymers,smart materials. For more details, You can visit : / @polymerscope6881
Пікірлер: 59
Thanks for sharing your valuable experiences
Hey! I know this is a weird question, but I need to make a grow-toy (lie the dinosaurs that grow in water) from scratch. I can't find any informatio on it other that it is made of "a mixture of sodium polyacrylate, polyvinyl acetate (a polymer used as a binder) and ethylene vinyl acetate". However, I have no idea how to make them. Could You please walk me through the process of making it from scratch? Is it even possible without a professional equipment?
I have some questions that I hope you can answer: 1/ What is the temperature of the solution after being divided and stirred before being placed in ice water? 2/ VSA put it in for the wrong purpose?
thanks the swelling ratio increases with an increase of VSA due to an increased in functional groups of SO3 in VSA are negatively charged polyelectrolytes in the polymerization medium; therefore, strong electrostatic repulsive forces hydrogel would be obtained that has a higher swelling capacity.
I am trying to prepare this hydrogel, without VSA. Here there is no mention of Nitrogen environment, which I frequently encounter while going through literature. It would be great if you can throw some light on it.
How to use these hydrogel like(alginate geletine) polymeric hydrogel for biological applications like antimicrobial, anti cancer etc.....
@sonalkhaitan469
9 ай бұрын
Hello you are on?
Please send the link of research article so I can download and understand more
@polymerscope6881
Жыл бұрын
Modeling of Swelling Behaviors of Acrylamide-Based Polymeric Hydrogels by Intelligent System doi.org/10.1080/01932691.2014.996892
how did you fixed temperature at 10 during polymerization reaction?
Hello sir may i know standard dimensions of hydrogel using for compression and tensile purpose .
Why didn't you vary APS AND TEMED in the different mixtures professor?
@polymerscope6881
Жыл бұрын
It can also be used like this after a homogeneous mixture is provided. it is best to prepare their aqueous solutions beforehand.
I'm trying to make a polyacrylamide gel (that has Triton X for increased hydrophilicity), but the surface keeps swelling/wrinkling. How would I keep it smooth?
@polymerscope6881
Жыл бұрын
If the polymerization reaction is slow, it will have a smooth surface.
hello Prof., I can find APS, can I use Sodium persulphate?
@polymerscope6881
11 ай бұрын
Yes
Sir what we can say that the water convert into gel and what we can use this gel as glue or Polymer or as Binder
@polymerscope6881
Жыл бұрын
You need a hydrophilic crosslinker.
Is there another alternative chemical I can uses to substitute VSA?
i can't find APS, can I use Sodium persulphate?
@polymerscope6881
11 ай бұрын
Yes.
Please share the recipe or refer ur article related to nanoparticles incorporated hydrogel of geletine alginate...
@polymerscope6881
11 ай бұрын
I think the answer is on google. There are many articles
@yogitabasnal
10 ай бұрын
@@polymerscope6881 but in google they are saying they are not stable and after sometime it corrodes, no stable incorporation method is available at this time.
Thanks for sharing this video.I have a question,Can I add chitosan with PEI (polyethylenamine)to this mixture?Thank you.
@polymerscope6881
Жыл бұрын
Of course you can add. However, since the ionic power balance will change, there will be differences in swelling values.
@hesamkasraie6820
Жыл бұрын
Thanks for your reply.Can I have your email address?
can you synthesize sodium polyacrylate
Is there need to add APS , if we are using PNIPAm?
Pls let me know this hydrogel can use as a plant watering applications
@polymerscope6881
2 жыл бұрын
U should synthesis crosslinked polypotassium acrylate by this method. This good plant watering agent.
After checking their swellability , is it possible to get their original texture and shape restored?
@polymerscope6881
10 ай бұрын
Yes
@gemsofdigitalworld
10 ай бұрын
@@polymerscope6881how?
@yogitabasnal
10 ай бұрын
@@polymerscope6881do we need to use heavy stone to break the glass tube?? Because the small pieces of test tubes. Stick to the hydrogel when the glass test tube cracks 😢
Sir... Kindly share the video of making cost effective hydrogels
@cihangirboztepe5918
3 жыл бұрын
Such as Acrylamide, acrylic acid or another? What kind you want?
@deepajessi2510
3 жыл бұрын
Thank you for your reply sir... I need acrylamide gel sir
@hakkozgurkaya8822
3 жыл бұрын
@@cihangirboztepe5918 sizi facebook dan ekledım uygun olduğunuzda dönüş yaparmısınız
Hi!, I would like to know the process of synthesizing hydrogel powder or spheres?.. I am trying to develop one out of novel materials. Hope you can help me..Thankyou!
@polymerscope6881
2 жыл бұрын
The details shown in this bro.
@luckyandreibautista5270
2 жыл бұрын
@@polymerscope6881 A'ight man
Does ethanol as solvent instead of DI water effect acrlyamide hydrogel formation ?
@polymerscope6881
Жыл бұрын
Sure it does affect. The yield of the polymerization reaction is very low.
@shivimaurya9631
Жыл бұрын
Sir the chemical used is not soluble in DI water bt in ethanol...so is there any way to get the polyacrlyamide gel little viscous gel using ethanol ?
@polymerscope6881
Жыл бұрын
@@shivimaurya9631 The less you use crosslinker MBAAm, the more fluid it will be. For example, if you use the crosslinker at 0.2 mole percent of the monomer, you can get a viscous gel.
@shivimaurya9631
Жыл бұрын
Thank you sir for the valuable suggestion😊
how to buy APS?
@polymerscope6881
Жыл бұрын
From Chemicals companies (Sigma Aldrich etc. )
those highy swellable are for what purpose? because as far as i know too much swellability is not prefered in vivo in humans because it puts too much pressure in the nearby tissue and increases tension. Are those swellable well suited for agriculture??
@T--xo2uq
7 ай бұрын
Swelling is also bad for applications in batteries which is what I'm interested in... I've seen one paper that used cellulose as the copolymer, I'm trying to figure out the rest of their process, i.e. amount of AA monomer added.
@yogitabasnal
7 ай бұрын
@@T--xo2uq as far as I have observed, the hydrogels which are synthesized at higher temperatures are more swellable like at more than 60 degrees but the ones synthesized at 41 degree around are less swellable. Highly swellable can found applications in agriculture for sure
@kunalsinha52
4 ай бұрын
I am trying to prepare this hydrogel, without VSA. Here there is no mention of Nitrogen environment, which I frequently encounter while going through literature. It would be great if you can throw some light on it.
@yogitabasnal
4 ай бұрын
@@kunalsinha52 nitrogen purging is required to expel entrapped air/oxygen. Some people also use argon for the same. Its not mandatory though. I synthesized my hydrogels without nitrogen purging and they were synthesized really well.
Are you a biomedical engineer?
@polymerscope6881
Жыл бұрын
No, I am Chemical Engineer. But my field of study is related to biomedical engineering.
Acrylamide Hydrogel