This is the first video i can finally say " YOU NAILED IT", i've been strugglling for months with my anycubic photon mono x because i could not find the right spot for printing small details and your set up worked PERFECTLY, i am trully gratefull for the information you shared and you got a new follower. THANK YOU MAN!

Just want to let you know I've had a printer for about a year and have had alot of trouble I watched this video today and changes stuff around and had a fantastic print thank you so much.

I'm new to resin printing and this was PERFECT for me. Thank you so much!!!

Just the info I've been looking for! I'm anxious to watch your other videos and continue learning. I have a Photon Mono SE, and have been struggling to get my prints to come out correctly with no "perfect" luck.

I was about to give up with resin printing. This has helped me start to actually understand things so Im starting again..Thanks !

Going to be trying out your suggestions and dial in my printer and resin! Thanks for the very clear instructions!

that’s a very good idea to use a microscope for analysis, thanks for the tips! 🙂

@RonPerron

2 жыл бұрын

Great vid. But wear gloves with uncured prints!!

Being new to 3D printing, I found your video very helpful. Thank you.

This is tons of great info, and the ResinLapse looked *amazing*! 👍

@3DMakerNoob

3 жыл бұрын

yes it was, even though you might be biased on that 😂

@AndrewSink

3 жыл бұрын

@@3DMakerNoob Maybe just a little bit! 🤣

This is a great video. Your communication is brilliant

This is exactly what I needed to figure out why my prints didn't look quite right, thanks!

best video for settings out there, hopefully we can get an updated video regarding this.

Just a note, holes in the resin exposure test can be perfect if you decrease the "bottom exposure time" in your slicer because this is a small flat object and the printing time is just few minutes (only for this test) and much easier to remove it from the build plate

Love this! Thank you!

I'm waiting my Photon Mono SE arrives, your information will be very useful to get fast and correct prints, thanks a lot! I'll buy Anycubic resin, it seems very correct resin

Bloody great informative video that was to the point and easy to understand. It is a sub from me and can’t wait for your vid on lift speeds. Top instruction mate thanks.

This is awesome video! thanks for making this

Thank you so much for this valuable Video. What did you use for initial exposure for the [ Siraya Tech (Navy Grey)] ? I can see you elaborated on layer exposure which helped me a lot as I own the same printer and same resin. However, my concern is the initial exposure.

Thank you for an amazing tutorial! Could you please tell me what UV power % are you using

What about the UV power setting?

Very cool thanks for sharing.

Excellent Joe. I learned so much in this video. I think I'm finally ready to use my Photon. Thank you.

Great video! I want to get into resin printing as soon as I move to another apartment with more rooms. This video will really help me get started Keep this amazing content coming 👍🏻

Struggling like crazy to get a decent set up for Elegoo ABS grey on my mono x. I'll give this a go. Everything comes out with super thick supports!

@LlethanderDrae

2 жыл бұрын

Having the same issue with Elegoo ABS-Like Grey on my Mono X. I've settled on 2.6s exposure with 40mm/min lifting speed but feel like it's a bit overexposed due to detail loss in smaller areas like faces and such.

Awesome video! I feel the same way about my FDM game...after spending so many hours with it, I just "GET IT". I know exactly what to do and what to adjust in order to create a great print. Honestly, I can say that I attribute that to learning from my mistakes and those of others. MORESO the mistakes of others though. KZread has been an invaluable tool for the 3D printing community. There just aren't enough people out there documenting their workflow and findings in the Resin Printing world and I feel that this is one of the reasons why we aren't seeing as many Resin 3D Makers as we have FDM Makers. I've been sitting with a Photon Mono (and all the fixins' to make printing easy, EX...Wash and cure station...flex plate) but have only managed to get about 1 kg of resin through the vat because troubleshooting isn't quite the same. Once I get a little extra time I will be going through this video and trying what you've recommended. Thank You For The Great Video!

Props to you for advertising at 14 dollar USB microscope instead of a 200 dollar one and taking a cut. I've tried maybe a dozen of them with that basic form factor and they're all pretty much exactly the same.

@3DMakerNoob

3 жыл бұрын

It’s useless spending a ton of money for such things. I bought mine 2 years ago and never used it, purely because I thought one day it could come in handy

Could you explain others settings for speeds, distances and other things?thanks a lot

thanks for the Video ! Csn i ask you something? I just bought my first 3D printer (anycubic photon mono x) and the testcube printed fine...then i had just failures...then i tryed some presupported figure and it worked again...the next day everything failed again multiple times...the first layers Stick to the plate just fine but afterwards it connects to the vat....i tried some exposure times already but its always the same result

Can you print individual parts? Like print the torso/head/arms solo so you can maximize the size and therefore print larger overall statues??

Could you please explain why you add 0.4 seconds to your exposure time in regards to the z axis. Whats the theory behind that? How are you coming up with that number and how does the exposure correlate with the z axis in any way? Is not the movement of the build plate the restricting factor? If it only move up 50micron there is only 50 mikron space for the resin to cure along the z axis, no? And how is the z axis not taken into Account in the first print?

@killer00zz

2 жыл бұрын

exacly! i want to know to i think its not necesery.

@bluediablito

2 жыл бұрын

Just spent some time reading all the comments to see if there is any explanation on the .4 seconds and nothing. Does anyone know why .4 was added?

@FallenFeyArts

2 жыл бұрын

Agreed. This makes no sense to me.

Can you explain why the .4 extra seconds and correlation with Z?? Trying to figure out that part please

Hello, can you do a tutorial for UV Tools with the mono x please? :)

I love the smoothness of resin printing but I am surprised at the lack of strength! Great informative video though!

@3DMakerNoob

3 жыл бұрын

I’ll have some videos on strength. You’d be surprised at how better it can be than FDM when you start mixing certain resins :)

@krissebesta

2 жыл бұрын

Look into Siraya Blu v2. Very strong resin.

nice vid ..once you got the exposure right and the swatch is 99 percent mint .skys the limt ram them speeds up 250 plus and they well print ive noticed. then its all about your surpports settings then ..and resin prints take so long if you dont give them a little help lol

What do you mean by increasing for Z axis ? I cannot find anything about that elsewhere

what was the power of the uv lamps for the test? 100%, 80%, 65%? this is critical to compare. regards

@krissebesta

2 жыл бұрын

I agree with you. I'd like to know his uv power level but in theory we can follow the steps he has outlined and dial in our resins. I am going to be running my uv light at 80%. Cheers!

@aidanfordsword6954

2 жыл бұрын

@@krissebesta I think some different types of resin have a suggested percentage but I'm not sure

@noway8233

2 жыл бұрын

I was thinking that, well uv ligth power goes from 65 to 80% , then yuo can play with it, ie. Print at 65% uv power and 2.0 sec, then compare the same but 80%

Great video and love that resinlapse clip

Do you know if different exposure times have any effect on strength?

Thanks.

thanks, this explains it in terms i can understand. the shortest version is get a checker pattern equal on uncured and super clean print. i use ultrasonic

which slicer would you recommend? do you think the photon workshop is any good?

That's awesome! I got some siraya tech blu, but went through a different process of dialing in the resin. This would have been a lot less costly than the way that i did it. Thanks for the great video!

I'm using Photon Mono X for dental application please send the settings for anycubic standard resin . Apart from chittubox is there any other software for mono x model ?

Thank you. I learned a lot!

this test is better first or before the cure under UV light for the resin??

thank u

I for some reason have gotten better prints with stuff that is 1 second or less using the XP2 test. I am kind of alarmed because every other place suggests around 1.8-2 seconds for the elegoo standard grey. I also was using the 4 layers.

@briankelly2580

Жыл бұрын

same my exposure using anycubic basic grey is 1.3 seconds

Just got the Anycubic Photon Mono X and eSun Hard Tough Resin. On Photon Workshop I setup a new Resin Profile for eSun Hard Tough Resin: Layer 0.05 Exposure 2.4 Off-time 4 Bottom exp 30 sec Bottom layers: 4 z-lift: 4mm Saved to stick. While running the file, I went into the Set Up screen on the machine and it shows different values: Exposure: 8 sec Off-time: 1 sec Bottom exp: 60 sec Bottom layers: 3 Looking at the time between lifts it seems that it follows the latter. So I had to adjust on the fly. Even then I'm still seeing the lifts happen about 12 sec in between. I'm totally confused. Please help.

Hey there I just got Anycubic photon mono x printer I am using Anycubic 3D Printing UV Sensitive Resin basic Grey, I am using lychee slicer any idea where I can find the resin profiles, I am total newbie never owned a 3D printer of any kind.

thx u Great

Can you print individual parts? Like print the torso/head/arms solo so you can maximize the size and therefore print larger overall statues?? Im asking bc this will be my first 3d printer and want to know if i can maximize the size by individually printing the parts

@bmann78

2 жыл бұрын

Yes you can. Most people do this unless they're printing minis.

How did you get chitubox to recognise the Anycubic photon mono …. I have the x2 but no support for it

My first resin printer is on order, I guess it time to start learning 3D printing *AGAIN* lol

@3dbatman126

2 жыл бұрын

same here

Great video!

Hi; I needed your information about a subject I was wondering about. I have a mono x machine. When I print with different layer thicknesses, for example, I don't have a problem with "0.05", but when I print at "0.1" with the same model, same settings and same support settings, it turns out to be problematic, with different layer thicknesses. Is it necessary to change the print and support settings or can such problems occur due to mono x? thanks.

@3DMakerNoob

2 жыл бұрын

Different layer heights require different setting, such as exposure time and also support joint sizes as it impacts it a lot

Very great video. Hope to see more of resin printing from you soon.

@3DMakerNoob

3 жыл бұрын

That’s the plan :)

i know this is over a year old but how do you use Chitutbox , save slice files in the pwmx format? oi have ver. 1.7.0 cuz i'm broke

so 2.4 exposure is best?

i dont understand what you mean at 8:18

Man, I really want to expand into Resin printing.

what is a good uv power % for the mono x for translucent resin?

@3DMakerNoob

Жыл бұрын

I’d say 80% should be more than enough

Thanks for the great tips! I have heard so far that you should not touch uncured prints as they can still cause allergies. However I see you are touching them with bare hands so I was wondering what is your take on it?

Hello, im in contact with Anycubic trough a ticket, but i think there not understand me. i was wonder if you can do test for me on your Mono X with the Resin XP2 Validation calibration test, do just a dry test, no VAT and no buildplatform attached, just make 1 bottom layer with 30 seconds exposure time and the normal layer at 1.65 seconds. so i was wonder if your printer do just 1 layer at 30 seconds and then starts the second with 1.65 and all other layers too.. my printer just start and arround layer 3 or 4 its reduse the exposuretime and by layer 10 orso it starts with 1.65 seconds... so it is not work the given settings that is in the PWMX file that is made.. i tested the same settings at a Mono and then its do 1 layer at 30 seconds and then starts right away with 1.65 seconds.. Anycubic told me that the printer do make transitions in layers but i think its a fault in my printer.. could you try that on your printer.. to see if it will do just 1 bottom layer at 30 seconds and then go further at 1.65 seconds.. and you can then easy see it on the TFT screen.. because its a dry test.. so no resin is need for this simple test. I hope you can help me out.. im get crazy of it.. have my printer for weeks now and even not get a good print out of it.. oh .. and before i forgot, you have great video's good learing ones and nice tips etc :) i have here a video about my Mono X and you can see very good that it is not work that file commands: kzread.info/dash/bejne/q5eBlZuhnZrPebg.html Best Regards Mark

@krissebesta

2 жыл бұрын

I have the same printer but have not started using it yet. I have heard that this printer automatically puts down 10 layers before printing the object. I wish it didn't do this either. Also, can you check to see if your bed is perfectly level and let me know? My bed is slightly higher around the outer edges (perimeter on all 4 sides) by 0.5 mm. I was expecting the bed to be perfectly flat so I want to know if I need to grind/sand it flat before I start using it.

@ArthA122

2 жыл бұрын

@@krissebesta I sanded mine with 80grit on a flat stone surface (marble countertop). Works perfectly now

why did u pass the curing process?

You should also take a look at the other photonsters project UVTools Resin Exposure finder

What if you have used this but only the circles appear and nothing else does and all the other detail dont even form

@jay_r9825

2 жыл бұрын

Late reply but Lack of details is usually a sign of over exposure try lowering your exposure time

I´ve bought one just like yours, but one thing that bothers me is that the printed samples strongly smells resin for too many days. Is that normal? I´ve not cured the sample not even washed with ethanol after printed...

@aidanfordsword6954

2 жыл бұрын

Sorry if I didn't understand the comment, but did you wash it? And or cure it? Because if you didn't do any of those steps its still gonna smell like resin for a while. If you did wash it, then try either washing it for a little longer (if you got the wash and cure machine from any cubic) or so end a little more time with a too the brush on the model.

@mcavalcantesouza

2 жыл бұрын

@@aidanfordsword6954 thank you for answering. Yes, you understood precisely my question. I tried to wash it for a longer periodo, but it persists smelling resig... not as strong as before, but still smells. I've heard that maybe it is happening due to the resign brand. Thank you again!!

You did not tell anyone how to change the exposure setting on the machine or when you have the program on your computer. I have test print failure with no idea what to change on the machine to complete the prints for test.

hi Guys, so do you just print one at a time changing the exposure settings for each or can you print all of them at the same time? I am a little confused at how this works but its quite interesting. Thanks,

@aidanfordsword6954

2 жыл бұрын

One at a time I'm pretty sure.

@dr679

2 жыл бұрын

@@aidanfordsword6954 thank you

dunk your model into hot water before removing the supports, makes it a lot easier to remove

@SirJamesIGamerfuzion

3 жыл бұрын

agree

@krissebesta

2 жыл бұрын

Do you clean it with ipa first then warm water? I've heard a blow dryer works well too.

@Pendrayk

2 жыл бұрын

@@krissebesta yes, clean off the resin with IPA bath and then dunk II not hot water to soften the resin to help remove the supports. Don't make it too hot though. You need to be able to put your hand in without boiling your own flesh of the bone :)

@Pendrayk

2 жыл бұрын

Also don't keep it in got water to long just 3 or 4 seconds. You can always redunk it if there are a lot of supports to remove

@krissebesta

2 жыл бұрын

@@Pendrayk Excellent! Thanks!

5:16 ish. pretty sure you should always cure your prints for health reasons. certainly need to wear gloves when handling uncured resin, even if you've cleaned a lot of the excess liquid off.

can you comment your UV percent on this please! all the info is useless without that!

@3DMakerNoob

2 жыл бұрын

It doesn’t matter what I’ve percentage I am running as each machine coupled with the type of resin will yield different result. I’d start with 80% and work your way up

No entendí nada

@xXDIVINOXx

2 жыл бұрын

estoy buscando setting para mi photon mono x y estoy sufriendo con el ingles..

+++++++++++++++

Hello sir please make a giveaway of a 3D Printer. Better if you giveaway Creality CR10 V3 3D Printer

In my opinion, this test is too imprecise. The results must be evaluated subjectively. That's too imprecise. Try TableFlip Foundry's "Cones of Calibration". This test leaves no room for interpretation. I test every resin with it, and always have unequivocal results. The download includes a PDF with a short explanation. Have fun

Pssst..... might wanna look into logos before printing the swirls are known and published peto marks according to FBI just FYI

@3DMakerNoob

3 жыл бұрын

Wouldn’t know as I don’t do research for such things. An infinity symbol is an infinity symbol

Excellent video!