1934 Simple Bioplastic Made Stronger Than Steel
Don't forget to check out Luke's channel found here / @tntomnibus
If you want to have a look at those special videos become a member and join by clicking this link / @thinkingandtinkering
Don't forget to check out Luke's channel found here / @tntomnibus
If you want to have a look at those special videos become a member and join by clicking this link / @thinkingandtinkering
Пікірлер: 226
Body armor out of milk vinegar and a pencil. Nice
@drillerdev4624
Жыл бұрын
McGyver seal of approval.
@grinningtiki220
Жыл бұрын
That would make a great Dr. Stone episode
One more step into the realm of Bio-Armor, nice!
@antoniopacelli
Жыл бұрын
What about making it Bio- Reactive..‽ All without making it a Symbiont...
@AndreaDingbatt
Жыл бұрын
@@antoniopacelli😮🤔😁😎👍👍
@jameszietsman5518
Жыл бұрын
Soon, we'll have to protect RMS from those men in dark suits!
@AndreaDingbatt
Жыл бұрын
@@jameszietsman5518 💞😎👏😅💞👍👍
I have been after duplicating these same video from 7 years ago for a while now, and thanks to this I know I am on the right track for most of it. Since I do not need to clean out the soap agent, I will be seeing if I can get this to do similar levels with LDPE shreds. I can get shopping bags all day long, so if I can turn them into a high strength material, I can make all kinds of things with it.
Thank you Rob for once again showing us how outside the box thinking can solve some incredibly difficult problems! The moment I saw you mention the uses for graphene powder, it made me think of ROMAN concrete. I was going to ask, now that we know the exact formula for the toughest long lasting Ancient Roman Concrete, would it be possible to reinforce the ancient Roman Formula with graphene powder, for Concrete that can be put to work for DIY dams or seaside projects? It would be self sealing and could withstand the fall of time itself.
Wow! I always saw casein mixed with formaldehyde to make plastic. This is a much better option. Great video Rob!
You Just Keep Getting More INCREDIBLE
Casein is pretty useful on its own. When combined with 4+ layers of linen it makes Linothorax armour as used by the ancient Greeks. Note linen or hemp has to be used rather than cotton because of the microstructure of the vegetable fibres. So-o-o- how would your casein graphene perform?
@Buzzhumma
Жыл бұрын
Aliens have already got this tech and anti tech . That's where rob got it from . You see👍🏻
@schwadevivre4158
Жыл бұрын
@@Fgway Linothorax is fibre reinforced plastic and the linen/hemp fibres are woven and not as brittle as glass or kevlar.
@makinganoise6028
Жыл бұрын
People have made reproduction linothorax armour and tested with arrows, blades etc, it was used for a long time, it is pretty effective, needs a lot of linen though, but at a time when metal was scarce it did a great job, plus it wasn't as hot as wearing metal in a hot Mediterranean climate, truth is we don't know how many layers, or how it was made, if glues or leather were also part of the layers or if casein was part of the process.
@DrJohnnyApocolypse
8 ай бұрын
That’s amazing thank you for sharing I had no idea, I was already thinking of making a composite plate from hemp, using 20-40 layer high density hemp weave canvas.. being that hemp has such amazing properties, it is already being held up to Kevlar as a viable replacement but I had no clue this was already done in ancient times, I saw hemp soft armor from ancient Asia but never heard of this ancient composite plate. Also want to look into weaves that spread more energy in more directions, there’s a standard plain weave (2 directions) but there’s also triaxial and quadraxial weaves (3 & 4 directions) which is more costly but drastically stronger with any material, they make triaxial carbon fiber for high strength parts in aerospace and performance racing So my new idea is a bio plastic hemp composite ballistic plate, triaxial weave or quadraxial, every other layer cut tilted to 5 degrees, bioplastic impregnated with graphine powder & microfibers for strength as well as ammonium polyphosphate for flame resistance
@CraigLandsberg-lk1ep
Ай бұрын
@@DrJohnnyApocolypseso glad to read your comment, saw it mths ago but couldn't find it again till now 😅😅
Wow! Thus could be very useful in so many ways. I wonder about the durability over time, exposure to UV, etc. Thank you for sharing these results with us! You never fail to amaze with your creativity!
Taking us through the drying process would be amazing.
Love the segment rob. Reminds me of my days in science class when we made "milk glue". Can't remember exactly what went into it other than milk but it was tough as nails. It was used to hold air craft together during the war when materials were scarce😮
@OriginalMorningStar
Жыл бұрын
Borax was added to make a woodworkers glue. Or salt water to make a delicious Mozarella cheese... In the Middle Ages, plain soil was added to make a 'cheese floor', smooth and hard as concrete, and could be polished to a shine.
@archibaldvonkranski8881
Жыл бұрын
@@OriginalMorningStar cheese...... Is there anything it can't do😍❤️❤️
I was just amazed to see the video open with stock footage of my own neighborhood!
They did similar thing on Tech Ingredients channel here on YT a few weeks ago where they made pure graphene then laced some epoxy resin with it. As in this video it was astonishing the small amount they added made a big increase in the material strength under load. Very interesting subject thanks.
Awesome work man!!!!!!!! I had almost forgot you did a video about this 7 years ago. What you have made is incredible!
I remember when you were talking about graphene infused plastic years ago and I'm glad to see another update! I'm curious about the strength testing, specifically I'd be interested in seeing the results, what method was used, which measure of strength shows that it's stronger than steel, etc, and I'm curious as to how much the graphene contributed to that strength. I did a quick search that implied that casein is normally on the order of 100 times lower ultimate tensile strength than steel, so if the graphene improved the strength by a factor of 100 or more then that's huge... Thanks again for sharing all the work you do and I'm looking forward to more updates!
I am wondering about increasing strength of epoxy resin for coating plywood in boat building. I think you mentioned adding to resin in a previous video. Anyway, as you probably know there are lots of beaches where coming ashore is not exactly like a tropical beach of pure white soft sand. A lot of places in Florida and the Gulf coast of Texas are sharp oyster or reef zones east to damage a boat’s hull. If this stuff can stop a bullet it can sure add protection to a hull moving at less than 10 knots coming aground. I’m thinking add to epoxy on rudder blade, centreboard and centreboard case. Also wondering about UV aspects. Epoxy has zero UV protection and needs paint or UV varnish out in the sun. I’m in Australia : it’s almost winter but I still need a hat and sunglasses outside during the day. Anyway just amazing videos.
Quite remarkable. Well done!
Beautiful, thank you! I knew graphene would help, but a strength-to-weight at 10x metal is astounding!
I wonder if you can mix 0.5% of this stuff whit PLA+ and extrude it for printing or if it whould slowly obstruct the nozzle. If some one have a filament extruder it's worth a shoot i think.
@kmcderm133
Жыл бұрын
I kept thinking: I want this to be 3D printable! :D
@ScarletFlames1
Жыл бұрын
I think there already exists plastics with graphene in them, I remember the downside is that it chews on the tip of the extruder (aka, the bit that prints the plastics). But I'm unsure of how well bonded it is as it's not pressed under 2 tons lol
@chaorrottai
Жыл бұрын
I haven't seen graphene pla but there's lot of carbon nanotube pla
@Buzzhumma
Жыл бұрын
Well it's a lubricant so I would think it wouldn't clog the nozzle unless it got wet .
@Erbmon
Жыл бұрын
turns out there are loads of academics pappers on this... should have started there. If someones is curius betwen 0.1 and 0.2 are the ideal ratios the load goes up around 45% tensile stenght by 17% and energy absortion to about 12% prety neat.
In the middle ages leather shields were impregnated with hide glue because that made an extremely though composite, they are incredibly strong and though.
Good heavens the durability on that thing genuinely scares me. Does this stuff decay over time? If not, this stuff could probably be used in some long term applications like buildings. Very cool!
1:11 The youtube tutorial song killed be, thank you for existing, never change !
The problem for us DIY'ers is the combo of heating + pressure. It takes expensive equipment to do this, and making such equipment is not easy either. I suppose you could use all metal vices to push down on it and heat it in an oven or the like, but I don't think that would do near as good as the equipment in the video, and especially not compared to what industry can use/do. With that said, this material would be very interesting to combine with either carbon fiber, basalt fiber, and/or S2 fiberglass cloths and epoxy composite outer, since I'm pretty sure the casein is not fully waterproof. Encasing the bioplastic composite in an epoxy-fiber composite, should make it even stronger, tougher, and completely waterproof. The bioplastic composite would be an *excellent* bulking agent since casein is pretty low density. Would love to see composite blends between the above for all kinds of things from car panels, skateboards, etc, etc.
Excellent and you gave a shout-out to Tech ingredients another must watch channel.
Is that basically dried grated cheese with grapevine added... when I have bits of cheese stuck to the pot after making it, it goes incredible hard, so I must remember to wash early. :)
Milk does grow strong bones! That’s amazing! I’m curious to know what strength parameters were tested? Compression? Tension? Shear?
I feel like I know all I need to live through the apocalypse by watching your vids. Thanks!
Mold parts of a normally be made of metal. For cars such as an engine block massively rerducing weight. An incredible strength!
Neat. Milk proteins to make the graphene and milk proteins to make the plastic.
So cool! It's Strange how everything's starting to fall in the place we spent years in this community researching. Graffiti and how to make it and all the sudden. It was like a key was found to the lock and now we can move forward with very interesting projects. The bioplast guy agree has great potential for body armor I will be giving this a go!!
Today I learned that can make laser with "dye" too, growable microbial dye, if we can move to custom microchip that would be complete!
So basically graphene infused dried cheese, very cool.
I've seen people create home made extrudes for recycling failed 3D prints and print supports, I wonder if you could make a bio-plastic 3D printer filament with this? That might give rise to stronger 3D printed parts (could be useful for wind turbine blades.
interesting that the process for this plastic is not unlike teflon, where they powder it and press it in a mold while heating in the pressurized mold to get the shape. Seems like making friends with a shop that does machining of plastics could prove useful as you could take the chips and shavings and then grind them up to make the powder that graphene is added to before pressing to get that shape out of any plastic similar, (especially the ones that cant be just heated and flow like we do with 3D printer filament plastics)
Can you do something more quantitative, like comparing it to a similar sized piece of mild steel in an hydraulic press or sheer tester?
Gear molds or actual gears made from graphene.
Thank you for the video!
Just a thought someone may be able to explore. Some bio-plastics shrink as they cure. A particular mix of concrete that allowed for a graphene incorporated plastic to cure could maybe be pretensioned by default? Just a thought
@Yezpahr
Жыл бұрын
I honestly don't think shrinkage is a problem with this specific mix and manufacturing process... It's put under a 20 ton press and is already highly compressed due to that. If we put it in a concrete mold that has the 20 ton force needed to mold, then you still need 20 tons of force to keep the mold in place and get all the product inside. I'm more curious what happens to the conductivity, can this perform like metal in more than one way? What if we press a wire out of this, would it be floppy or would it be brittle, ready to snap when you look at it wrong?
@ricksanchez3176
Жыл бұрын
@@Yezpahr Sincerely, either I'm not understanding you, or you're not understanding me? The shrinkage in the case would not be a problem, rather a problem turned into a benefit. It wouldn't have to be this plastic, but any that the graphene would bond to. If part of the curing process would utilize the solvent shed by the plastic curing, maybe, only maybe, it would be possible to have a lattice reinforced concrete. There are many videos on pre and post tensioned concrete and it's benefits, if that is where we're not seeing each other. Kinda a Rupert drop, but a block, and not largely the surface.
That's one more giant leap for mankind !
I was going to say it looked like your camera was vintage 1934 too!
Looks like I missed this video 6 days ago. Happy to watch it now though . The reminiscent sound quality of 6 years ago was also apparent . I recall the other plastic enhancement of some years back . I think polystyrene dissolved in acetone with the Graphene also in solution then letting the acetone evaporate away to result in enhanced polyester plate with super tuffness .
An all biodplastic pistol! The Possibilities are limitless!
If that was able to be dispensed into a 3d printer you'd have something amazing, not that it's not already.
@TheBaconWizard
Жыл бұрын
I reckon you could just do it. If you use the UV liquid resin type printer, just add graphene to the resin!
@user-um9sl1kj6u
Жыл бұрын
The problem with a 3-D printer is that it’s just Layering hot plastic that’s not very dense at all (it can’t) 3-D printer is good for one offs, modeling, and maybe knickknacks here and there that aren’t really anything you need to rely on. They’re good in a pinch, but that’s basically it. If you were really in trouble, we’re just wanted to make an at home robot, toy, or something that you do not mind breaking Sintering metal, Or other composites, is another matter entirely.
@Gomorragh
Жыл бұрын
@@user-um9sl1kj6u they also just said resin printer not plc printer, that more crystalline growth type layering with a surface coat to make it smooth
@geoffkeller5337
Жыл бұрын
@user-um9sl1kj6u It depends on the type of 3D printer. There are a lot of different versions out there that are making fantastic, usable, and long-lasting items... not just trinkets or one-offs.
@djagrarms7916
Жыл бұрын
@@geoffkeller5337 agreed the technology is definitely there, on a consumer level the easily printable polymers with all the qualities we want at a acceptable price is probably a little bit further down the road.👍🏼
Would love to see the results of mixing graphene & high density foam.
From Green Tea Graphene about eight years ago, and now Graphene from blood, eggs and milk. Hmm.. if you find somewhere, a way to make Graphene from flour, we can take all the leftovers and have afternoon tea with cakes and blood pudding! 😂 And maybe you'll be known as the Graphene Gourmet! hahahaha! Cheers Robert!
@draganmiletich3013
Жыл бұрын
Potato starch?
@Charlie-Oooooo
Жыл бұрын
@@draganmiletich3013 Brilliant! 80c for 3 hours seems to do it for the reduction of Graphene Oxide to Graphene! Research revealed that corn powder works too. How about mini potato pancakes and/or corn muffins. Delicious! 👍😄
You could industrialize the process and make giant panels like wallboard panels. You put them in underneath the drywall to make a bullet proof house!
more videos of this please!! cheers
My head! It is reeling from too much potential. I’ll be able to start my own Space program soon! Thanks to this Tinkering man, I’ll be on the Moon by the Time I reach 90.
Tony Stark technology. Impressive!
I just imagine that this material layered in a strong fiber and resin / epoxy base, formed on a concave curved outside edge mold for a chest plate, would make an excellent dragon scale 🐉 armor, especially for blocking spalling bullet fragments. Spalled Fragments from any bullet can riddle large blood vessels in the arms, neck and face. ☠
So if I just drink it I'll also become bullet proof - awesome!
Bulletproof Cedar style shingle. For exterior of home to make your home bulletproof?
Somewhere inside all of us there is a world class prepped looking to go public 😂🎉
Brilliant. mate!
yes, very very much a perfect video.
More explanations about what makes it so strong would be nice. Is there a specific chemical reaction happening in there ?
the indestructible Shed coming up with a lightweight graphene reinforced foundation
You could make a copy of that vest your wearing with it and test how bullet proof it is. Now you just need a volunteer. Any takers?
Thats insane
You could make electric cars from it 100% from bumper to bumper. Even the battery technology could have graphenei in it made from bio plastic!
Casein, isn't that what's in my coffee creamer?
I have a plated armor vest. I'm thinking about making plates for that purpose. Put it in there and test it to see it's bullet resistance..
So for the same protection as steel, you only need half the thickness, and it will be a fifth of the weight. Make a trowel.
Mike about gained a new hole a couple different times while wielding that screwdriver
I would be really surprised if there weren't a few companies around the world desperately trying to figure out how to shut down your channel because of what knowledge you're sharing. Thank you Rob! Keep it up.
Kitchen science at it's best! How does the Graphene affect the other properties of the plastic? I'm thinking of heat and elasticity. I keep wondering when you are going to run out of twists to "normal" stuff ........ but I guess the answer to that is "Never"! Once again Thanks for all this output!
Does it have to be compressed? Can this be turned into a thermoplastic for 3d printing?
That stuff would be a good choice for making a watch case.
Did you add .5% by weight or by volume? BTW this is some great stuff. Many thanks for pioneering and sharing to inspire us!
@Rem_NL
Жыл бұрын
he usually weighs by molar or weight
@that_escalated_quickly2720
Жыл бұрын
@@Rem_NL thank you! Cheers
@MachineLordZero
10 ай бұрын
@@Rem_NL Thankyou
Would you be willing to produce some in varying thicknesses for some American gun you tubers to test on firing ranges against different hand guns and rifles ?
Thats quite amazing. How does it stand up to different temperatures and water? Could imagine myself casting items out of such a material. If added to epoxy would it be as strong?
Wow I wonde if it can't be pressed onto a sheet of kevlar or something, to make it even stronger, and easy to sew on to a vest, if not I'm sure it can be epoxied on to kevlar, a ship lap pattern would probably do nicely, having a puck 3mm thick on both sides, overlapping with a couple layers of denim and kevlar between you and it, on the back side , looks like it would stop nearly anything you are likely to be hit with!
You could make. Reinforced bbs for shotgun ammo making its armor piercing shotgun rounds.?
the 20 tons of pressure is a small limitation for diy purposes
So we can make bullet proof vests from milk which is great but how is this linking back to your wind turbines if at all? I really am more interested in your wind turbines but I do find this stuff fascinating as well. 👍
so cool, have a wonderful day!
So we used whey for the first part and curds for the second part. Little Miss Muffet would be pleased.
Hi. So i wonder if it is posible to somehow add this solution to a 3d peinter so make the plasic even stroger. Sorry for my english
Mate ,Fantastic! Cheers! What if the powder was first blended with the milk? Have you tried that yet?
Very cool
Have you given any thoughts to making a 3 principal filament from the biocason? You could. Make Body. Armor specific to a particular body type and shape.then print it in a dragon scale mail armor? Mabe?
WOW 🤯 I ish I had a press to make some panels out of this stuff!
I'd be curious to see if it could be used as 3d printing filament. Imagine 3d prints being stronger than steel.
@hunakosdem
Жыл бұрын
Heeey, this is a genius idea!
How can I get the graphene you use? I'd love to see you do a bullet-proof vest and test it out.
Hi my friend I been with you so long I call you a part of my world and family It’s great to be able to text you Shame you don’t live in door You and your show is absolutely excellent thank you so much for your time and effort
And now, we are in for some cooking lessons, at least what I thought in at the beginning of this and previous episode/lesson 🙂
What about it keeping it's shape, thermal capacity, will it degrade quickly?
Fire an arrow at it, with a sharp hunting head and a bodkin, see how it compares to kevlar, steel plate, ceramic, a book! Or if feeling really adventurous make linothorax, a bullet and stabproof backpack can be made cheaply with some tiles and a few books, dont test at home children.
I feel so inspired just seeing this, but with an eye to the possible future, and a view of the mistakes we have made in the past; if we had invested in this tech all along, would we have a fix for getting rid of things we had made from it if they were past their most useful? We have the huge problem of plastic waste today because we never thought it through properly. Can we do better this time? I do hope so. This stuff seems so strong, I am not sure how we could go about disposal if needed. Thanks for the insight of course, I am not trying to put any kind of downer on this concept, quite the opposite, just trying to have the answers before others try and spin it away because they have a vested interest in the old polluting petrochem style that is plaguing us right now. Be well. 😉
Could you cast the windmill parts with it? I wasn't sure if that would work because of the press. Thinking along the lines of using the 3d printed parts, maybe printed out of pva fiber as a positive mould to make the negative mould.
Crazy awesome. So we take some milk, boil it, add it to vinegar, separate out the casein. Then mix in graphite with the leftovers and liquidise. Would the vinegar affect the ability of the proteins keeping the graphite granules separated? What size centrifuge would be needed to separate the graphene? Could it just be boiled off? So many questions. It would be worth a few hours of my time trying to find the answers. Thanks!!
Just thinking out loud, Would it make a good bearing?
a women in a high heel shoe the heels can damage soft wood floors and ground can damage heels.
Caseine? I thought you made Mozzarella using milk & vinegar...
Would that stop a Taser?!!🤔 Not planning on getting Tasted,Lol 😆 I think that it would stop the initial things that'd hit us,,, ~ but Graphene is conducive though...?! Brilliant Video as Always Robert, Many thanks from Carlisle, Andréa and Critters. ...XxX...
@TheAce736
Жыл бұрын
In the case it conducts with the plastic it'll just complete the circuit that way, rather than jumping in and out of your body, I assume.
@AndreaDingbatt
Жыл бұрын
@@TheAce736 Thank You!!😎👍👍 I'm not sure if I will get to testing this theory,,,, But,it is the memory of my eldest Sister who said "Hold my hand while I hold onto this Electric Fence."!! Ooouchaaaa!! I'm not sure why this memory surfaced when Robert's video came on!?!!🤔😁 Namasté 🙏💞 Andréa and Critters. ...XxX.....
Is it still electrically conductive?
Send some to Demolition Ranch.
I often think about experiments with electro culture for growing vegetables etc . Not sure how I would go about it other than mix the graphene in the soil around the roots of the planst to assist in the conductivity . Do you know about electro culture Rob ?
@johnmcfadden9336
Жыл бұрын
I can see the possibility that antennae could be made graphene coated instead of copper but I’m not sure it is viable to mix with the soil or even desirable, there is a lot of talk about graphene and graphene oxide I the vaccines that are said to be harmful, it’s not something I know much about but caution might be advised
@Buzzhumma
Жыл бұрын
@@johnmcfadden9336 yeah well that's true mate . Maybe just conductive carbon mixed through the soil to allow more efficient pathways for the electron . I guess being the size that it is , It could easily end up in the actually produce and then consumed . 🤷♀️
So you can just blend your milk with graphite to make graphene and then turn it into plastic composite in one go as you make the bio plastic.
Graphene einforced bioplastic roofing shingles?
Could this be made to be a healthy tooth filling? Casein + biochar + pine resin?